通过单辊急冷法和铜模铸造法制备出新型Ti基金属玻璃Ti53Cu27Ni12Sc3Al7Si3B1.用DSC、DTA分析其热稳定性,XRD分析晶化前后相组成.结果表明:用铜模铸造法可以制备出最大直径为2mm的完全玻璃相棒材,其Tg、Tx、⊿Tx分别为729K、765K和36K,具有较高热稳定性.力学性能测试表明其具有较高的力学性能,压缩断裂强度、弹性模量和压缩塑性变形量分别为2325MPa、118GPa和1.6%.具有明显的弹塑性变形阶段.
参考文献
| [1] | Tanner L E;Ray R .[J].Scripta Materialia,1977,11:783. |
| [2] | Polk D E;Calka A;Giessen B C .[J].Acta Materialia,1978,26:1097. |
| [3] | Tanner L E;Ray R .[J].Acta Materialia,1979,27:1727. |
| [4] | Inoue A;Masumoto T;Suryanarayana C et al.[J].Journal de Physique,1980,41(08):758. |
| [5] | Zhang T;Inoue A;Masumoto T .[J].Materials Science and Engineering,1994,A181-A182:1423. |
| [6] | Amiya K;Nishiyama N;Inou A et al.[J].Materials Science and Engineering,1994,A179-A180:692. |
| [7] | Inoue A;Nishiyama N;Amiya K et al.[J].Materials Letters,1994,19:131. |
| [8] | suryanarayana C;Inoue A;Masumoto T .[J].Journal of Materials Science,1980,15:1993. |
| [9] | Zhang T;Inoue A;Masurnoto T .[J].Materials Letters,1993,15:379. |
| [10] | Zhang T;Inoue A .[J].Materials Transactions,1998,39:1001. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%