以Y2O3、Nd2O3、Al(NO3)3·9H2O、(NH4)2SO4为原料,分别采用碳酸氢铵和碳酸铵两种沉淀剂,通过共沉淀法制备了YAG超细粉体.采用热重-差热分析(TG-DTA)与红外光谱(IR)对前驱体进行分析研究.对不同温度下煅烧的粉体进行X射线衍射(XRD)与透射电镜(TEM)分析.研究结果表明:采用碳酸氢铵作为沉淀剂得到的前驱体经1000 ℃煅烧可获得纯YAG相,颗粒尺寸为60～150 nm;而采用碳酸铵作为沉淀剂得到的前驱体经900 ℃煅烧即可获得纯YAG相,颗粒尺寸较小,约为40～50 nm,具有良好的分散性.
参考文献
| [1] | Ikesue A.;Kamata K.;Furusato I. .FABRICATION OF POLYCRYSTALLINE, TRANSPARENT YAG CERAMICS BY A SOLID-STATE REACTION METHOD[J].Journal of the American Ceramic Society,1995(1):225-228. |
| [2] | Sim S M;Keller K A .Phase fomation in YAG powder synthesized by chemical methods[J].Journal of Materials Science,2000,35:713-717. |
| [3] | Hakuta Y;Seino K;Ura H et al.Production of phosphor (YAG:Tb) fine particles by hydrothermal synthesis in supercritical water[J].Journal of Materials Chemistry,1999,9:2671-2674. |
| [4] | Li J G;Ikegami T;Lee J H et al.Co-precipitation synthesis and sintering of yttrium aluminum garnet powders:the effect of precipitant[J].Journal of the European Ceramic Society,2000,20:2395-2405. |
| [5] | 李霞,刘宏,王继扬,崔洪梅,张旭东.钇铝石榴石透明激光陶瓷的研究进展[J].硅酸盐学报,2004(04):485-489,506. |
| [6] | 丁志立,陈嵩,韩杰才.柠檬酸法、氨水沉淀法和碳酸氢铵沉淀法制备的钇铝石榴石纳米粉体性能的比较[J].硅酸盐学报,2005(03):380-385. |
| [7] | 丁志立,陈嵩,韩杰才.以碳酸氢铵为沉淀剂制备纳米钇铝石榴石粉体[J].材料工程,2005(02):48-50. |
| [8] | 郭旺,卢铁城,仝世红,张颖,邹萍.共沉淀法制备纯相钇铝石榴石（YAG）纳米粉体中的若干影响因素[J].功能材料,2006(01):66-69. |
| [9] | 万艳芬,曹全喜,李双春,李珍,苏董杰.Nd：YAG激光陶瓷纳米粉体的制备方法研究[J].传感技术学报,2006(05):2365-2368. |
| [10] | 赵郝炎,廖梅松,胡丽丽.热处理对共沉淀法制备YAG纳米粉体性能的影响[J].人工晶体学报,2006(02):395-399. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%