以三聚氰胺、间苯二酚、甲醛为原料,采用溶胶-凝胶法、冷冻干燥等步骤制备出三聚氰胺-间苯二酚-甲醛( MR)干凝胶；并以所制炭气凝胶为载体浸渍硝酸钴,经氮气中高温炭化,得到钴复合氮掺杂的炭气凝胶。考察间苯二酚和三聚氰胺比例、凝胶pH值及炭化条件等对气凝胶结构和催化氧还原活性的影响,采用XRD、XPS、低温氮气吸脱附等方法研究催化剂的结构。随pH值增加,MR气凝胶的介孔分布向小孔移动；当M/R物质的量比为6：1时,其介孔分布为3.0~4.0 nm。钴复合炭气凝胶多孔结构中存在均匀分布Co金属颗粒和管状炭,Co金属颗粒粒径随炭化温度升高而增加。采用旋转圆盘电极研究催化剂在0.5 mol/L H2 SO4溶液中的电化学性能,结果表明催化剂具有良好的氧还原活性。
Melamine-resorcinol-formaldehyde ( MR) aerogels were prepared by the sol-gel polymerization of formaldehyde with melamine and resorcinol using NaOH as catalyst, followed by freeze-drying. Co-loaded carbon aerogels were obtained by impregna-ting the MR aerogels with Co( III) tert-butanol solution, followed by carbonization in N2 . The effects of the molar ratios of mela-mine to resorcinol ( M/R) , pH, Co content and carbonization temperature on the microstructure of the aerogels were investigated. It was found that the microstructure of the MR aerogels could be adjusted by the M/R ratio and pH. The mesopore size of the MR aer-ogels decreased with increasing pH and the mesopore size was in the range of 3-4nm when the M/R was 6:1. There were some gra-phitic nano-ribbons in Co-loaded carbon aerogels. The metal average particle size in the carbon aerogels increased from 5. 2 to 6. 2 nm when the carbonization temperature was increased from 700 to 900℃. The electrochemical properties of the Co-loaded car-bon aerogels as catalysts in the oxygen reduction reaction were evaluated by a rotating disc electrode technique in an O2-saturated 0. 5 mol/L H2 SO4 solution, and the catalysts showed a good electrocatalytic activity for the reaction.
参考文献
| [1] | Pekala R W;Alviso C T;Kong F M et al.Aerogels derived from multifunctional organic monomers[J].J Non-Cryst Sol-ids,1992,145(1-3):90-98. |
| [2] | 钱旦,郝广平,李文翠.含氮多孔炭的制备及其在二氧化碳吸附中的应用[J].新型炭材料,2013(04):267-272. |
| [3] | C. Medard;M. Lefevre;J. P. Dodelet;F. Jaouen;G. Lindbergh .Oxygen reduction by Fe-based catalysts in PEM fuel cell conditions: Activity and selectivity of the catalysts obtained with two Fe precursors and various carbon supports[J].Electrochimica Acta,2006(16):3202-3213. |
| [4] | Siyu Ye;Ashok K. Vijh .Non-noble metal-carbonized aerogel composites as electrocatalysts for the oxygen reduction reaction[J].Electrochemistry communications,2003(3):272-275. |
| [5] | Siyu Ye;Ashok K. Vijh .Cobalt-carbonized aerogel nanocomposites electrocatalysts for the oxygen reduction reaction[J].International journal of hydrogen energy,2005(9):1011-1015. |
| [6] | Yang Wei;Chen Shengzhou;Lin Weiming .Oxygen reduction on non-noble metal electrocatalysts supported on N-doped carbon aerogel composites[J].International journal of hydrogen energy,2012(1):942-945. |
| [7] | Donghui Long;Jie Zhang;Junhe Yang .Chemical state of nitrogen in carbon aerogels issued from phenol-melamine-formaldehyde gels[J].Carbon: An International Journal Sponsored by the American Carbon Society,2008(9):1259-1262. |
| [8] | 龙东辉,张洁,杨俊和,胡子君,李同起,成果,张睿,凌立成.苯酚-间甲酚-糠醛基炭气凝胶的制备及微结构控制[J].新型炭材料,2008(02):165-170. |
| [9] | 张睿,李雯,胡子君,张琢,高楠,钱惠春,凌立成.蜜胺-酚醛树脂-甲醛基有机气凝胶纳米孔在裂解过程中的稳定性研究[J].新型炭材料,2009(01):23-27. |
| [10] | 李良伟,陈胜洲,林维明.间苯二酚对三聚氰胺-甲醛碳气凝胶催化剂的影响[J].电池,2012(03):129-131. |
| [11] | Maldonado-Hodar FJ.;Rivera-Utrilla J.;Hanzawa Y. Yamada Y.;Moreno-Castilla C. .Catalytic graphitization of carbon aerogels by transition metals[J].Langmuir: The ACS Journal of Surfaces and Colloids,2000(9):4367-4373. |
| [12] | Biniak S.;Siedlewski J.;Swiatkowski A.;Szymanski G. .THE CHARACTERIZATION OF ACTIVATED CARBONS WITH OXYGEN AND NITROGEN SURFACE GROUPS[J].Carbon: An International Journal Sponsored by the American Carbon Society,1997(12):1799-1810. |
| [13] | Zielke U.;Hoffman WP.;Huttinger KJ. .SURFACE-OXIDIZED CARBON FIBERS .1. SURFACE STRUCTURE AND CHEMISTRY[J].Carbon: An International Journal Sponsored by the American Carbon Society,1996(8):983-998. |
| [14] | Zhu Q.;Russell AE.;Thomas KM.;Money SL. .DETERMINATION OF THE FATE OF NITROGEN FUNCTIONALITY IN CARBONACEOUS MATERIALS DURING PYROLYSIS AND COMBUSTION USING X-RAY ABSORPTION NEAR EDGE STRUCTURE SPECTROSCOPY[J].Langmuir: The ACS Journal of Surfaces and Colloids,1997(7):2149-2157. |
| [15] | J. R. PELS;F. KAPTEIJN;J. A. MOULIJN;Q. ZHU;K. M. THOMAS .EVOLUTION OF NITROGEN FUNCTIONALITIES IN CARBONACEOUS MATERIALS DURING PYROLYSIS[J].Carbon: An International Journal Sponsored by the American Carbon Society,1995(11):1641-1653. |
| [16] | Shang Li;Lei Zhang;Jenny Kim;Mu Pan;Zheng Shi;Jiujun Zhang .Synthesis of carbon-supported binary FeCo-N non-noble metal electrocatalysts for the oxygen reduction reaction[J].Electrochimica Acta,2010(24):7346-7353. |
| [17] | Adina Morozan;Stephane Campidelli;Arianna Filoramo .Catalytic activity of cobalt and iron phthalocyanines or porphyrins supported on different carbon nanotubes towards oxygen reduction reaction[J].Carbon: An International Journal Sponsored by the American Carbon Society,2011(14):4839-4847. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%