Ceramic coatings were deposited on 2Al2 alloy with a 100 kW micro-arc oxidation equipment consisting of a potential adjustable ac power supply and alkali electrolyte. The structure of the micro-arc oxidiation coatings was examined using scanning electron microscopy and transmission electron microscopy. The tribological properties of the coatings sliding against steel under the drop and adsorption lubrication of liquid paraffin were evaluated with a Timken tester. The lower friction coefficient of 0.14 and longer wear life of 2450 m of overcoat were observed for the polished micro-arc oxidation coating of 180μm thick at a sliding speed 2. 50 m/s and load 1500 N. This is because the coating has an interlayer of suitable porosity and thickness, which helps to improve the deposition of lubricants and endure the higher load. In other words, the oil is able to adsorb in the porous holes of the overcoat and provided the lubrication of micro reservoir during friction, and the compact and relatively hard interlayer of oxidation coating is able to support heavy load and prevent the oil lubricating film from damage.
参考文献
| [1] | Kurze P;Krysmann W;Schreckennach J et al.[J].Crystal Research and Technology,1987,22:53. |
| [2] | VanT B;Brown S D;Wirtz G P .[J].American Ceramic Society Bulletin,1977,56:563. |
| [3] | Krysmann W;Kurze P;Dittrich K H et al.[J].Crystal Research and Technology,1984,19:973. |
| [4] | Schreckenbach J .[J].Metallober flache,1991,45:437. |
| [5] | Malyschev V .[J].Oberflachentechnik,1995,49:606. |
| [6] | Dittrich K H;Krysmann W;Kurze P et al.[J].Crystal Research and Technology,1984,19:93. |
| [7] | Kurze P;Krysmann W;Schneider H G .[J].Crystal Research and Technology,1986,21:1603. |
| [8] | Xue WB.;Lai YC.;Chen RY.;Deng ZW. .Analysis of phase distribution for ceramic coatings formed by microarc oxidation on aluminum alloy[J].Journal of the American Ceramic Society,1998(5):1365-1368. |
| [9] | Heintze G N;Uematsu S .[J].Surface and Coatings Technology,1992,50:213. |
| [10] | XueWB;DengZh W;Chen R Y et al.[J].Thin Solid Films,2000,372:114. |
| [11] | Tian J.;Luo ZZ.;Qi SK.;Sun XJ. .Structure and antiwear behavior of micro-arc oxidized coatings on aluminum alloy[J].Surface & Coatings Technology,2002(1):1-7. |
| [12] | Xue WB.;Chen RY.;Zhang TH.;Ma H.;Deng ZW. .Microstructure and properties of ceramic coatings produced on 2024 aluminum alloy by microarc oxidation[J].Journal of Materials Science,2001(11):2615-2619. |
| [13] | Nie X.;Meletis EI.;Jiang JC.;Leyland A.;Yerokhin AL.;Matthews A. .Abrasive wear/corrosion properties and TEM analysis of Al2O3 coatings fabricated using plasma electrolysis[J].Surface & Coatings Technology,2002(2/3):245-251. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%