研究了ZM5铸造镁合金微弧氧化过程中膜生长规律和膜的相结构及形貌特征,并探讨了氧化膜生长机理.在初始一段时间内,氧化膜向外生长速度大于向内生长速度.氧化膜达到一定厚度后,工件外部尺寸不再增加,而氧化膜完全转向基体内部生长.氧化膜具有表面疏松层和致密层2层结构,在NaAlO2溶液中氧化时,前者由MgO和MgAl2O4相组成,后者主要由MgO组成.疏松层中富集来自溶液的铝元素.
参考文献
| [1] | Malyschev V .Microarc Oxidation[J].Metallober flache,1995,49(08):606-607. |
| [2] | Kurze P .Magnesium Alloys Electrochemical Coatings[J].Metallober flache,1994,48(02):104-105. |
| [3] | Zozulin A J;Bartak D E .Anodized Coatings for Magnesium Alloys[J].Metal Finishing,1994,92(03):39-43. |
| [4] | Xue WB.;Lai YC.;Chen RY.;Deng ZW. .Analysis of phase distribution for ceramic coatings formed by microarc oxidation on aluminum alloy[J].Journal of the American Ceramic Society,1998(5):1365-1368. |
| [5] | 薛文斌;邓志威;来永春;汪新福 .Formation Process and Properties of Ceramic Coating Formed by the Microarc Oxidation on Aluminum Alloys[J].电镀与精饰,1996,18(05):3-6. |
| [6] | 薛文彬,邓志威,来永春.LY12铝合金微弧氧化的尺寸变化规律[J].中国有色金属学报,1997(03):140-143. |
| [7] | 薛文斌;来永春;邓志威;陈如意 .The Properties of Coating Formed by Microplasma Oxidation on Magnesium Alloy[J].材料科学与工艺,1997,5(02):89-92. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%