介绍了一种类网状结构的多孔态泡沫钨及其制备方法.该泡沫钨材料的孔隙分两类:(1)是构成类网状结构且孔径为0.2~1.0mm的主孔;(2)是存在于主孔孔壁和孔棱之上且孔径在几个微米量级的微孔.主孔呈通孔和半通孔结构,并且两类孔隙相互连通,总孔率高于50%.该泡沫钨的制备方法是以有机泡沫材料为基体,采用浸浆干燥烧结法制备而成.其中料浆由钨粉和无毒性有机黏结剂组成,黏度用去离子水调节.
A porous tungsten foam with net-like structure and the corresponding preparing method are presented in this paper. This tungsten foam has two classes of pores, one is the main pore constituting the net-like structure and having the diameter of 0.2-1.0mm, and the other is the tiny pore existing in the pore-wall of the main pore and the pore strut and having the diameter of several micrometers. The main pores show a connective or half-connective structure, and they are also connective to the tiny pores, with the overall porosity higher than 50%. This tungsten foam was prepared by organic foamed plastic matrix soaking the slurry and drying then sintering, with the slurry consists of the tungsten powder and the nonpoisonous organic agglomerant, and the viscosity adjusted by deionized water.
参考文献
[1] | 刘培生.多孔材料引论[M].北京:清华大学出版社,2004 |
[2] | 廖际常.低温烧结孔隙度可控多孔钨[J].稀有金属快报,2006(09):41-42. |
[3] | 滕修仁,张晗亮.影响多孔钨孔隙度的因素[J].稀有金属材料与工程,1998(06):379-380. |
[4] | Selcuk C;Wood J V .[J].Journal of Materials Processing Technology,2005,170:471-476. |
[5] | [OL].http://dlib.edu.cnki.net,1990-2008. |
[6] | ISI Web of Knowledge,1990-2008[M]. |
[7] | 刘培生,黄林国.多孔金属材料制备方法[J].功能材料,2002(01):5-8,11. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%