μSingle-crystal alpha alumina (α-Al2O3) platelets were synthesized by calcining a powder mixture of bayerite (α-Al(OH)3) and potassium sulfate (K2SO4) at 900°C. The crystalline phase evolutions and morphologies of the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The synthesized samples mainly consisted of single-crystal α-Al2O3 platelets with a diameter of 0.5-1.5 μm and a thickness of 50-150 nm. Moreover, with 3, 5, and 8 wt% (referred to the obtained alumina) α-Al2O3 seeds adding into the powder mixture of bayerite and potassium sulfate, the average diameter of α-Al2O3 platelets can be reduced to 450, 240, and 220 nm, respectively. It is found that the sequence of the phase transformation is the bayerite (α-Al(OH)3) →boehmite (γ-AlOOH) →γ-Al2O3→α-Al2O3. Further analysis indicated that K2SO4 can promote the phase transformation from γ-Al2O3 to α-Al2O3 and the formation of single-crystal α-Al2O3 platelets might be attributed to the liquid phase K3Al(SO4)3.
参考文献
| [1] | M. Kotoul, J. Pokluda, P. Sandera, I. Dlouhy, Z. Chlup and A.R. Boccaccini: Acta Mater., 2008, 56, 2908.[2 ] S.H. Lim, K.Y. Zeng and C.B. He: Mater. Sci. Eng. A, 2010, 527, 5670.[3 ] R.F. Hill and P.H. Supancic: J. Am. Ceram. Soc., 2002, 85, 851.[4 ] X. Miao and C.C. Sorrell: J. Mater. Sci. Lett., 1998, 17, 2087.[5 ] I. Wadsworth and R. Stevens: J. Mater. Sci., 1991, 26, 6800.[6 ] R.F. Hill, R. Danzer and R.T. Paine: J. Am. Ceram. Soc., 2001, 84, 514.[7 ] C.A. Shaklee and G.L. Messing: J. Am. Ceram. Soc., 1994, 77, 2977.[8 ] S. Hashimoto and A. Yamaguchi: J. Mater. Res., 1999, 14, 4667.[9 ] H.C. Park, S.W. Kim, S.G. Lee, J.K. Kim, S.S. Hong, G.D. Lee and S.S. Park: Mater. Sci. Eng. A, 2003, 363, 330.[10] Y. Wu, K.L. Choy and L.L. Hench: J. Am. Ceram. Soc., 2004, 87, 1606.[11] M.Wei, D. Zhi and K.L. Choy: Nanotechnology, 2006, 17, 181.[12] W.H. Gitzen: Alumina as a Ceramic Material, Columbus, OH, 1970.[13] X. Du, X. Su, Y. Wang and J. Li: Mater. Res. Bull., 2009, 44, 660.[14] H. Song and R.L. Coble: J. Am. Ceram. Soc., 1990, 73, 2077.[15] H. Song and R.L. Coble: J. Am. Ceram. Soc., 1990, 73, 2086.[16] W.A. Kaysser, M. Sprissler, C.A. Handwerker and J.E. Blendell: J. Am. Ceram. Soc., 1987, 70, 339.[17] M.M. Seabaugh, G.L. Messing and M.D. Vaudin: J. Am. Ceram. Soc., 2000, 83, 3109.[18] X. Su, S. Li and J. Li: J. Am. Ceram. Soc., 2010, 93, 1904.[19] S.C. Srivastava, K.M. Godiwalla and M.K. Banerjee: J. Mater. Sci., 1997, 32, 835.[20] N.S. Bell, S.B. Cho and J.H. Adair: J. Am. Ceram. Soc., 1998, 81, 1411.[21] X. Jin and L. Gao: J. Am. Ceram. Soc., 2004, 87, 533. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%