α-Ti-低碳钢爆炸复合结合层的组织

材料研究学报, 1995, 9(2): 186-189.

α-Ti-低碳钢爆炸复合结合层的组织

中南工业大学

西北有色金属研究院

关键词：爆炸复合 , bonding interface layer , amorphous , adiabatic shear band(ASB)

MICROSTRUCTURE OF BONDING LAYER IN EXPLOSIVE CLADDED Ti-MILD STEEL

YANG Yang , ZHANG Xinming(Central South University ofTechnology)LI Zhenghua , LI Qingyun(Northwest Institute for Non ferrous Metal Research) , null

Keywords： : explosive cladding , 界面结合层 , 非晶 , 绝热剪切带

借助透射电镜(TEM)研究了TA2-A3爆炸复合界面结合层的微观结构.结果表明:该层的“冶金结合”是通过局部熔化和扩散共同作用实现的,宽约为几十微米.由宽度在100nm内变化的;由熔区和非熔区组成的界面层及A3侧的热影响区、以显微带为特征的形变区、以及TA2侧的绝热剪切带(ASB)组成.ASB内的晶粒细比成100nm内的等轴晶.且其中位错密度很低.ASB内没有发生hcp→bcc转变亦无熔化迹象.界面层的熔区内为非晶和纳米级微晶;A3基体内有少量形变孪晶:TA2基体内有高密度且相互交叉的形变孪晶

The TA2/A3 explosive cladding interface layers have been studied by TEM technique. The results show that the "metallurgical bond" of the explosive-cladding is achieved by local melting and diffusion at the contacted surface. There are microcrystals and a

参考文献

[1]	LucienFTrueb．TransoftheMetallSociofAIME1968:242:10572GaninE,KomenY,WeissBZ．ActaMetall．1986:34:1473HammeschmidtM,KregeH．meyersMA．MurrLeds．ShockWavesandHigh-Strain-ratePhenomenainMetals,PlenumPress．NewYork．1981．9614Dor-RamY．WeissBZ．KomenY．ActaMetall,1979:27．14175LinseVD,LaiwangNS,JMet,1984:36(5):62Z

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网