采用电脉冲空化成功制备出超细镍磷合金粉体材料.研究了脉冲能量、反应温度和电极间距等工艺因素对镍磷合金粉体尺寸、形貌及收得率的影响.结果表明:镍磷合金粉体粒径可控制在80～500 nm范围内.反应初期,反应形核受脉冲能量(电压和脉冲次数)的控制,镍磷合金粉体颗粒数随脉冲放电能量的增大而增加;随反应时间的延长,脉冲空化导致镍磷合金粉体的反应被激活,溶液中镍磷粉体可自发形核、生长,直至反应完成.镍磷合金粉体颗粒尺寸受形核及长大过程的共同影响.通常,随脉冲电压和脉冲次数的增加、电极间距的减小、反应温度的降低和反应时间的缩短而非线性减小.
参考文献
| [1] | 王世敏;许祖勋;傅晶.纳米材料制备技术[M].北京:化学工业出版社,2002 |
| [2] | Ivo Michael Krausz .Cavitational Synthesis of Nanostructured Inorganic Materials for Enhanced Heterogeneous Catalysis[D].Worcester Worcester Polytechnic Institute,2002. |
| [3] | Mettin R;Luther S;Ohl C D .Lauterborn W,Acoustic Cavition Strucyures and Simulations by a Particle Model[J].Ultrasonics Sonochemistry,1999,6:25-29. |
| [4] | Margulis MA.;Margulis IM. .Contemporary review on nature of sonoluminescence and sonochemical reactions[J].Ultrasonics sonochemistry,2002(1):1-10. |
| [5] | Magdalena Popczyk;Andrzej Serek;Antoni Budniok .Production and properties of composite layers based on an Ni-P amorphous matrix[J].Nanotechnology,2003(2):341-346. |
| [6] | 王瑛,余水,俞宏英,孙冬柏.空化场中纳米镍磷合金粉体材料的制备[J].材料工程,2003(08):17-19,22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%