本文用X射线粉末衍射分析法测定了钇≤16.7at.-%成分区域内Y-Cu-Ni三元系合金相图的室温截面.截面中包含有4个单相区:称为α,β,ε,ω相区,5个两相区:α+β,α+ε,α+ω,β+ω,ε+ω;2个三相区:α+β+ω,α+ε+ω.X射线分析表明,钇在α在相中的最大固溶度约为2 Wt-%.
The room temperature section of the phase diagram of the ternary Y-Cu-Nisystem for Y≤16.7 at.-% has been determined by X-ray powder diffractionmethod.Four single-phase regions:α,β,ε and ω;five two-phase regions:α+β,α+ε,α+ω,β+ω and ε+ω;and two three-phase regions:α+β+ω and α+ε+ωare found in the section.X-ray analysis showed that maximum solubility of Y inα-phase is about 2 wt-%.