采用双酚A型WSR-615和缩水甘油胺型AG-80环氧树脂为基体,以Fe-Si磁性颗粒为填料,通过热压成型方法制备了高含量磁性Fe-Si颗粒/环氧树脂复合材料.研究了环氧树脂基体的玻璃化温度和冲击强度及Fe-Si磁性颗粒含量对Fe-Si/环氧树脂复合材料的冲击强度和磁化强度的影响及温度敏感性.研究结果表明:随着磁性颗粒含量的增加,Fe-Si/环氧树脂复合材料的冲击强度和磁性能增加.当磁性颗粒体积分数由54 vol%增加到66 vol%时,Fe-Si/环氧树脂的冲击强度和饱和磁化强度分别由4.03 kJ/m2和162.07 emu/g增加到7.16 kJ/m2和175.04 emu/g.Fe-Si/环氧复合材料在-60℃~140℃范围内的温度敏感性低,符合实际应用对复合材料稳定性的要求.
参考文献
[1] | 郝元恺,肖加余.高性能复合材料学[M].北京:化学工业出版社,2004:13-64.Hao Yuankai,Xiao Jiayu.High performance composite materials[M].Beijing:Chemical Industry Press,2004:13-64. |
[2] | Dobrza(n)ski L A,Drak M.Structure and properties of composite materials with polymer matrix reinforced Nd-FeB hard magnetic nanostructured particles[J].Journal of Materials Processing Technology,2004,157-158:650-657. |
[3] | McHenry M E,Willard M A,Laughlin D E.Amorphous and nanocrystalline materials for applications as soft magnets[J].Progress in Materials Science,1999,44(4):291-433. |
[4] | 刘献明,付绍云,肖红梅,等.聚合-热解法制备Co0.2Zn0.2Mn0.6Fe2O4纳米颗粒及其表征[J].金属学报,2006,42(5):497-499.Liu Xianming,Fu Shaoyun,Xiao Hongmei,et al.Preparation of Co0.2Zn0.2Mn0.6Fe2O4 nanoparticles by a polymer-pyrolysis route and its characterization[J].Acta Metallurgica Sinica,2006,42(5):497-499. |
[5] | Morimoto K,Niizuma E,Igarashi K.Preparation of fully dense Nd-Fe-B magnets using semi-processed HDDR powders[J].Journal of Magnetism and Magnetic Material,2003,265(3):345-351. |
[6] | 洪向东,许启明.宽温度、大功率微波铁氧体材料研究[J].材料开发与应用,2008,23(2):24-26.Hong Xiangdong,Xu Qiming.Wide temperature coefficient and high power microwave ferrite[J].Development and Application of Materials,2008,23(2):24-26. |
[7] | Shokrollahi H,Janghorban K.Soft magnetic composite materials (SMCs)[J].Journal of Materials Processing Technology,2007,189(1-3):1-12. |
[8] | Dobrza(n)ski L A,Nowosielski R,Przybyl A,et al.Soft magnetic nanocomposite with powdered metallic ribbon based on cobalt and polymer matrix[J].Journal of Materials Processing Technology,2005,162:327-330. |
[9] | Taghvaei A H,Shokrollahi H,Ghaffari M,et al.Influence of particle size and compaction pressure on the magnetic properties of iron-phenolic soft magnetic composites[J].Journal of Physics and Chemistry of Solids,2010,71(1):7-11. |
[10] | 田民波.磁性材料[M].北京:清华大学出版社,2001:1-21.Tian Minbo.Magnetic materials[M].Beijing:Tsinghua University Press,2001:1-21. |
[11] | Takada Y,Abe M,Masuda S,et al.Commercial scale production of Fe-6.5wt.% Si sheet and its magnetic pro-perties[J].Journal of Applied Physics,1988,64(10):5367-5369. |
[12] | 全国纤维增强塑料标准化技术委员会.GB/T 2571-1995中华人民共和国国家标准[S].北京:中国标准出版社,1995.The National Fiber Plastic Standardzation Technical Committee.GB/T 2571-1995 The international standard of the People's Republic of China[S].Beijing:China Standards Press,1995. |
[13] | John N A S,George G A.Diglycidyl amine-epoxy resin networks:kinetics and mechanisms of cure[J].Progress in Polymer Science,1994,19(5):755-795. |
[14] | 蔡宏洋,李刚,刘海洋.柔性胺T403对环氧树脂体系力学性能及交联密度的影响[J].玻璃钢/复合材料,2009(1):38-41.Cai Hongyang,Li Gang,Liu Haiyang.Effects of flexible amine T403 on the mechanic properties and crosslinking density in epoxy systems[J].Fiber Reinforced Plastics/Composites,2009(1):38-41. |
[15] | 冯青平,杨娇平,刘玉,等.聚丙烯酸酯改性环氧树脂的力学性能[J].复合材料学报,2012,29(3):9-15.Feng Qingping,Yang Jiaoping,Liu Yu,et al.Mechanical properties of epoxy systems modified by polyacrylates[J].Acta Materiae Compositae Sinica,2012,29(3):9-15. |
[16] | 何曼君.高分子物理[M].上海:复旦大学出版社,2007.13-17.He Manjun.Polymer physics[M].Shanghai:Fudan University Press,2007:13-17. |
[17] | He X Q,Zhang D S,Li H R.Shape and size effects of ceria nanoparticles on the impact strength of ceria/epoxy resin composites[J].Particuology,2011,9(1):80-85. |
[18] | Yang G,Fu S Y,Yang J P.Preparation and mechanical properties of modified epoxy resins with flexible diamines[J].Polymer,2007,48(1):302-310. |
[19] | 杨果,潘勤彦,潘皖江,等.柔性胺改性剂对环氧树脂力学性能的影响[J].材料工程,2006(5):16-20.Yang Guo,Pan Qinyan,Pan Wanjiang,et al.Influence of flexible amine modifier on mechanical properties of epoxy resins[J].Journal of Materials Engineering,2006(5):16-20. |
[20] | Society of Automotive Engineers.SAE J1711-MAR1999.Recommended practice for measuring the exhaust emissions and fuel economy of hybrid-electric vehicles[S].Washington,D C:SAE International,1999. |
[21] | 胡长征.粉末冶金方法制备高硅铁硅合金的探索性研究[D].武汉:武汉理工大学,2004:26-46.Hu Changzheng.Study on fabrication of high Si-content Fe-Si alloy by power metallurgy[D].Wuhan:Wuhan University of Technology,2004:26-46. |
[22] | 李世荣,官仕龙,吴莉.丙烯酸改性F-44环氧树脂及其光固化性能研究[J].热固性树脂,2001,16(1):1-4.Li Shirong,Guan Shilong,Wu Li.Production and property of F-44 epoxy resin modified with acrylic acid[J].Thermosetting Resin,2001,16 (1):1-4. |
[23] | Fu S Y,Feng X Q,Lauke B,et al.Effects of particle size,particle/matrix interface adhesion and particle loading on mechanical properties of particulate-polymer composites[J].Composites Part B-Engineering,2008,39 (6):933-961. |
[24] | Liang J Z.Quantitative description of interfacial strength in polypropylene/inorganic particle composites[J].Polymer Composites,2011,32(5):821-828. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%