通过对造成换流站光纤局部放电的原因进行分析，采用加强光纤等电位和接地处理，并在光纤表皮聚四氟乙烯材料中加入炭黑，研究解决换流站阀厅光纤局部放电问题的方法。结果表明：经过加强光纤等电位和接地处理，光纤表皮材料聚四氟乙烯经过炭黑改性后，光纤表皮材料和光纤材料的介电常数和电阻率相匹配，自由电荷在光纤表皮材料上的累积减少，释放速度加快，从而有效消除了光纤局部放电现象。
The cause of optical fiber partial discharge in converter station was analyzed. Through enhanc-ing the equipotential and grounding treatment of optical fiber, and adding black carbon into fiber PTFE surface material, we studied the solutions of optical fiber partial discharge problems of valve hall in converter station. The results show that after enhancing the equipotential and grounding treatment of fiber and adding black carbon into the fiber PTFE surface material, the permittivity and resistivity between the optical fiber and surface material is more matching, the accumulation of free charge on the suface material decreases, and the release of free charge speeds up, which can eliminate the fiber partial discharge phenomena.
参考文献
| [1] | 黄道春,魏远航,钟连宏,阮江军,皇甫成.我国发展特高压直流输电中一些问题的探讨[J].电网技术,2007(08):6-12. |
| [2] | 李立浧.特高压直流输电的技术特点与工程应用[A].,2005 |
| [3] | 于成龙,叶海福.高压脉冲电容器的直流局部放电绝缘检测[J].高电压技术,2006(06):5-8. |
| [4] | 赵畹君.高压直流输电工程技术[M].北京:中国电力出版社,2004 |
| [5] | 边姗姗,吴广宁,张血琴,李晓华,彭倩.Delta（t）法分析高压储能电容直流局放信号[J].高电压技术,2007(08):135-138,142. |
| [6] | 邱昌容;王乃庆.电工设备局部放电及其测试技术[M].北京:机械工业出版社,1994 |
| [7] | 张文亮,于永清,李光范,范建斌,宿志一,陆家榆,李博.特高压直流技术研究[J].中国电机工程学报,2007(22):1-7. |
| [8] | 牛海清,陈小林,A.Cavallini,G.C.Montanari,张尧.高压直流局部放电的试验研究及其放电源识别策略[J].高电压技术,2009(07):1641-1647. |
| [9] | 张宗喜,舒乃秋,曾宏,聂德鑫.高压直流滤波电容器直流局部放电的试验研究[J].高压电器,2010(09):43-47. |
| [10] | 国网电力科学研究院 .换流站阀厅光纤局部放电故障原因分析及治理措施[R].国网电力科学研究院研究,2013. |
| [11] | 国网电力科学研究院 .换流站2014年改造启动系统调试报告[R].国网电力科学研究院研究,2013. |
| [12] | 赵凯,党智敏.四针状氧化锌晶须/聚四氟乙烯复合材料的电气性能研究[J].绝缘材料,2011(03):49-52. |
| [13] | 马媛媛,郑晓泉,别成亮.高能电子束辐照对聚四氟乙烯电气性能的影响[J].绝缘材料,2009(04):53-56. |
| [14] | 颜录科,李炜光,高莉宁,孙增智.碳纤维/硫酸钡混杂增强聚四氟乙烯复合材料的研究[J].绝缘材料,2010(01):14-17,20. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%