利用UTM-2摩擦磨损试验机进行试验,考察了在PAO4基础油润滑下,不同温度条件下织构(不同面密度-ρt,5％、10％、20％和排列方式-θ=0、30°、60°、90°)对青铜表面摩擦性能的影响.结果表明:在PAO4基础油润滑下,在60℃和100℃工况下,相对于原始表面,织构增大了摩擦系数和磨损率,而在25℃和150℃工况下,表面织构对摩擦磨损的影响不明显;随着温度的升高,原始表面和各类型织构表面的摩擦系数与磨损率都是呈现先升高再降低的趋势,No.3(ρt=20％,θ=0)和No.5(ρt=20％,θ =60°)试样有着较好的耐磨性能.
Tribological properties of laser surface textured bronze with different textured parameters were tested on an UTM-2 friction and wear tester under the lubrication of PAO4 base oil at different temperatures.The results show that compared to the original surface,the textured surfaces increase the friction coefficient and wear rate at 60 ℃ and 100 ℃,respectively.However,at 25 ℃ and 150 ℃,the texture exhibits a little influence on friction and wear behaviour of the bronze.With the temperature increasing,the friction coefficient and the wear rate of the all tested samples increase at first,and then decrease.The textured samples with the textured surface density of 20％ and the angles between the dimples of zero and 60°have better anti-wear performance.
参考文献
| [1] | Cho, Minhaeng;Choi, Hae-Jin.Optimization of Surface Texturing for Contact Between Steel and Ultrahigh Molecular Weight Polyethylene Under Boundary Lubrication[J].Tribology letters,20143(3):409-422. |
| [2] | 李祖来;蒋业华;周荣;陈志辉;山泉.Cr的添加对WCp/铁基表层复合材料三体磨料磨损性能的影响[J].材料热处理学报,2014(1):17-21. |
| [3] | 胡天昌;丁奇;胡丽天.激光表面织构化对GCr15钢摩擦磨损性能的影响[J].摩擦学学报,2011(5):447-451. |
| [4] | G. Ryk;Y. Kligerman;I. Etsion.Experimental investigation of laser surface texturing for reciprocating automotive components[J].Tribology Transactions,20024(4):444-449. |
| [5] | Ulrika Pettersson;Staffan Jacobson.Influence of surface texture on boundary lubricated sliding contacts[J].Tribology International,200311(11):857-864. |
| [6] | Etsion F.State of the art in laser surface texturing[J].Journal of Tribology,20051(1):248-253. |
| [7] | Toshikazu Nanbu;Yoshiteru Yasuda;Kenshi Ushijima;Jun Watanabe;Dong Zhu.Increase of Traction Coefficient due to Surface Microtexture[J].Tribology letters,20082(2):105-118. |
| [8] | Ulrika Pettersson;Staffan Jacobson.Textured surfaces for improved lubrication at high pressure and low sliding speed of roller/piston in hydraulic motors[J].Tribology International,20072(2):355-359. |
| [9] | Xiaolei Wang;Koji Kato.Improving the anti-seizure ability of SiC seal in water with RIE texturing[J].Tribology letters,20034(4):275-280. |
| [10] | Manabu Wakuda;Yukihiko Yamauchi;Shuzo Kanzaki;Yoshiteru Yasuda.Effect of surface texturing on friction reduction between ceramic and steel materials under lubricated sliding contact[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20033/4(3/4):356-363. |
| [11] | 闫利文.微机械制造工艺及其应用[J].现代制造工程,2004(03):83-85. |
| [12] | 王斌;常秋英;齐烨.激光表面织构化对45＃钢干摩擦特性的影响[J].润滑与密封,2013(12):11-14. |
| [13] | 符永宏;汤伯虎;纪敬虎;张华伟;华希俊.微凹坑织构表面摩擦学性能的实验研究*[J].润滑与密封,2013(5):19-23. |
| [14] | Aviram Ronen;Izhak Etsion;Yuri Kligerman.Friction-reducing surface-texturing in reciprocating automotive components[J].Tribology Transactions,20013(3):359-366. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%