利用SEM、XRD和EDS研究Y对Ti45Al8Nb(at%)合金在900℃空气中的循环氧化行为的影响.实验结果表明,适量Y的加入显著提高了合金的抗循环氧化性.无Y合金300次循环后便出现了表层氧化膜脱落,而含Y的6个合金除Ti45Al8Nb0.1Y在氧化460 h后出现大面积脱落外,其余合金在1000次循环内均未出现明显脱落.Y的加入显著增强了氧化膜与基体之间的粘附性.但是加入过量Y,合金氧化膜内颗粒较大的Y<,2>O<,3>偏聚在晶界处,为O提供了扩散通道,使合金出现了严重的内氧化.
参考文献
| [1] | Kim Y W;Chan K S .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,40:1121. |
| [2] | Liu C T .[J].Materials Chemistry and Physics,1995,42:77. |
| [3] | Yamaguchi M;Inui H;Ito K .[J].Acta Materialia,2000,48:307. |
| [4] | Chen Guoliang;Sun Zuqing;Zhou Xing .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1992,153:597. |
| [5] | Shida Y;Anada H .[J].Corms Science,1993,35:945. |
| [6] | Yoshihara M;Miura K .[J].Intermetallics,1995,3:357. |
| [7] | Taniguchi S;Shibata T .[J].Intermetallics,1996,4:S85. |
| [8] | Huang Boyun;He Yuehui .[J].Intermetallics,1999,7:881. |
| [9] | Zhang Weijun;Chen Guoliang;Sun Zuqing .[J].Scripta Materialia,1992,28:563. |
| [10] | 张卫军 .Research of Ternary Nb-Ti-Al Intermetallic(Nb-Ti-Al三元系金属间化合物研究)[D].Beijing:University of Science & Technology Be ijing,1991. |
| [11] | 曲恒磊,周廉,魏海荣.静止空气中TiAl断续氧化动力学[J].稀有金属材料与工程,2000(01):8-12. |
| [12] | 闫蕴琪,王文生,张振祺,洪权,罗国珍,周廉,Zhou Lian.一种高性能TiAl金属间化合物[J].金属热处理学报,2000(03):1-5. |
| [13] | 李铁藩.High Temperature Oxidation and Hot Corrosion of Metal(金属高温氧化和热腐蚀)[M].北京:化学工业出版社 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%