首先比较了4种碳质还原剂对MgO的还原能力,得到的还原效果依次为：焦炭〉木炭〉活性炭〉石墨。选取还原最佳的焦炭作为还原剂进行正交实验,结果表明焦碳的粒度影响最大,其次是时间和碳配比,而温度的影响相对较小。另外,添加氟化钙（CaF2）可以加速MgO的还原,使之在较低温度下的还原率增加。在1500℃×1h时,添加3%（质量分数）CaF2的MgO还原率从67%提高到了99%,而在1400℃×1h时,添加5%CaF2的MgO还原率也达到91%。
The reducibility of four carbonaceous reducing agents selected for magnesia （MgO） were coke 〉 char- coal 〉activated charcoal〉graphite, primarily determined by reduction rates. With the optimal coke as a reduc- ing agent, the orthogonal experiment of MgO reduction was carried out. The results have showed that the parti- cle size of coke was most important, followed by soaking time, carbon content and least-important temperature. Moreover, the introduction of calcium fluoride （CaF2） into the reduction system can accelerate the reduction and therefore increase reduction rates at lower temperature. At 1500℃/lh, the reduction rate with 3%CaF2 in- creased from 67% to 99% and at 1400℃/lh that with 5% CaF2 up to 91%.
参考文献
| [1] | 殷建华.世界镁工业的发展与前景[J].世界有色金属,2005(07):58-66. |
| [2] | 于旭光,邱竹贤.镁工业生产及应用的现状和展望[J].材料与冶金学报,2003(03):189-192. |
| [3] | 黄西平,张琦,郭淑元,王功伟.我国镁资源利用现状及开发前景[J].海湖盐与化工,2004(06):1-6. |
| [4] | 徐日瑶.金属镁生产工艺学[M].长沙:中南大学出版社,2002:1-3. |
| [5] | 韩继龙,孙庆国.金属镁生产工艺进展[J].盐湖研究,2008(04):59-65. |
| [6] | 苏鸿英.镁冶炼工艺技术综述[J].世界有色金属,2009(07):30-31. |
| [7] | Geoffrey Brooks;Winny Wulandari .New Processes for Magnesium Production[D].The Australian State of New South Waces:University of Wollongong,2009. |
| [8] | Hansgirg F .Production of magnesium[P].USP:2582120,1952-01-08. |
| [9] | Warren G F;Cameron A M .Prodn of Magnesium by Car-bon Reduction of Magnesia-using Oxide and Carbide Slag of Magnesium,Calcium and Aluminium[P].European Pat:84201741.0,1985-07 03. |
| [10] | 钟胜 .氧化镁真空碳热还原研究[D].昆明理工大学,1998. |
| [11] | Li Rongti;Pan Wei;Masamichi Sano et al.Kinetics o1 Reduction of Magnesia with Carbon[J].Thermochimica Aeta,2002,390:145-151. |
| [12] | Lan Hong;Hong Yong Sohn;Masamichi Sano .Kinetics of carbothermic reduction of magnesia and zinc oxide by thermogravimetric analysis technique[J].Scandinavian Journal of Metallurgy,2003(3):171-176. |
| [13] | 李志华,戴永年,薛怀生.真空碳热还原氧化镁的热力学分析及实验验证[J].有色金属,2005(01):56-59. |
| [14] | Gar lvez M E;La zaro M J;Moliner R .Novel Activated Carbon-based Catalysts for the Selective Catalytic leduc-tion of Nitrogen Oxide[J].Catalysis Today,2005,102-103:142-147. |
| [15] | Li RT.;Wei P.;Sano M.;Li JQ. .Catalytic reduction of magnesia by carbon[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,2003(1/2):265-267. |
| [16] | Galvez ME;Hischier I;Frei A;Steinfeld A .Ammonia production via a two-step A1(2)O(3)/AlN thermochemical cycle. 3. influence of the carbon reducing agent and cyclability[J].Industrial & Engineering Chemistry Research,2008(7):2231-2237. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%