将TiO2与海藻酸钠充分混合配制成铸膜液,在玻璃板上刮膜,经钙离子交联制备TiO2/海藻酸钙(T/CA)复合膜,并对其进行扫描电镜、透射电镜和红外表征.研究湿态T/CA复合膜经过紫外辐照前后的力学性能,以及复合膜对甲基橙染料的重复降解性能.结果表明,T/CA复合膜的力学强度与降解前相差不大,海藻酸盐大分子虽部分降解但仍可以被钙离子交联生成与降解前强度相差不大的凝胶.分析了紫外照射前后复合膜力学性能不变的原因.该复合膜制备工艺简单,成本低,经过紫外照射后仍保持优良的力学性能,重复使用10次后还能达到第1次降解率的97.6％.
参考文献
| [1] | Roberto Scotti;Massimiliano D'Arienzo;Franca Morazzoni .Immobilization of hydrothermally produced TiO2 with different phase composition for photocatalytic degradation of phenol[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2009(3/4):323-330. |
| [2] | S.K. Papageorgiou;F.K. Katsaros;E.P. Favvas;G. Em. Romanos;C.P. Athanasekou;K.G. Beltsios;O.I. Tzialla;P. Falaras .Alginate fibers as photocatalyst immobilizing agents applied in hybrid photocatalytic/ultrafiltration water treatment processes[J].Water research: A journal of the international water association,2012(6):1858-1872. |
| [3] | 王星敏,傅敏,张桂支,李铃.ACF/TiO2光催化膜制备及其降解活性研究[J].西南师范大学学报（自然科学版）,2008(04):93-96. |
| [4] | 亓敬波,梁小平,姜锋,王雪,李建新,何本桥,王虹.纳米TiO2/聚酯织物的制备及光催化性能[J].高分子材料科学与工程,2013(02):169-172,177. |
| [5] | 彭湘红,杜金萍,程德翔,陆茜,吕凡林.纳米二氧化钛/壳聚糖复合膜的光催化性能[J].化学与生物工程,2008(05):13-15,19. |
| [6] | 宋远卿,杨海刚,徐守斌,张见玲,江龙,淡宜.溶胶-凝胶法制备H-PVA/TiO_2复合膜及其可见光催化活性[J].高分子材料科学与工程,2012(02):140-143. |
| [7] | 梁文耀,罗颖,董先明,禹筱元.PEO改性纳米TiO2/LDPE复合薄膜的光降解性能[J].高分子材料科学与工程,2012(08):38-42. |
| [8] | Albarelli, JQ;Santos, DT;Murphy, S;Oelgemoller, M .Use of Ca-alginate as a novel support for TiO2 immobilization in methylene blue decolorisation[J].Water Science and Technology,2009(4):1081-1087. |
| [9] | 吴子豹,黄妙良,杨媛媛,林建明,吴季怀.负载型TiO2复合材料对甲基橙的吸附行为及光催化降解动力学[J].精细化工,2007(01):21-26. |
| [10] | Jeong-Yun Sun;Xuanhe Zhao;Widusha R. K. Illeperuma;Ovijit Chaudhuri;Kyu Hwan Oh;David J. Mooney;Joost J. Vlassak;Zhigang Suo .Highly stretchable and tough hydrogels[J].Nature,2012(Sep.6 TN.7414):133-136. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%