采用脉冲射频等离子体聚合方法在不锈钢基底上制备了聚烯丙胺薄膜,红外光谱和X射线光电子能谱分析表明:烯丙胺单体经脉冲等离子体射频放电所制备的聚合薄膜均含有胺基(-NH2) 官能团.低占空比的聚合薄膜中所含的-NH2浓度增多,薄膜的亲水性提高.薄膜的聚合速率随占空比的增加呈先增大后减小的规律.聚合薄膜与不锈钢基底间结合力也随着脉冲占空比的增加,呈先上升后下降的变化,且占空比为60%时具有最大的膜基结合力.
参考文献
| [1] | 赵华侨.等离子体化学与工艺[M].合肥:中国科学技术大学出版社,1993:255. |
| [2] | Hamerli P;Weigel T;Groth T;Paul D .Surface properties of and cell adhesion onto allylamine-plasma-coated polyethylenterephtalat membranes.[J].Biomaterials,2003(22):3989-3999. |
| [3] | Morraa M;Cassinelli C;Cascardo G et al.[J].BIOMATERIALS,2003,24:4639-4654. |
| [4] | Puleoa D A;Kisslinga R A;Sheu M S .[J].Biomaterials,2002,23:2079-2087. |
| [5] | Zhang J;Feng X F;Xie H K et al.[J].Thin Solid Films,2003,435:108-115. |
| [6] | Choukourov A.;Biederman H.;Slavinska D.;Trchova M.;Hollander A. .The influence of pulse parameters on film composition during pulsed plasma polymerization of diaminocyclohexane[J].Surface & Coatings Technology,2003(0):863-866. |
| [7] | 潘长江,黄楠,刘睿睿,王进,孙鸿.不同有机单体等离子体聚合的对比研究[J].高分子材料科学与工程,2005(02):89-92. |
| [8] | Toshihiro H;Chie T .[J].Thin Solid Films,2004,45:720-725. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%