Two kinds of high pure silver materials with 5.3 ppm oxygen and 32.7 ppm oxygen were prepared by various melting processes,both samples were subjected to accumulative rolling with 95％ thickness reduction.Their mechanical properties were tested during long natural aging.Results showed that the Ag sheet with 5.3 ppm oxygen is at full annealed state when natural aging 58 days or kept at 150℃ for 30 minutes,and the Ag sheet with 32.7 ppm oxygen is a little of recovery when natural aging a year.It is suggested that appropriate oxygen interstitial solute in Ag solid solution and a few of Ag2O particles at Ag grain boundaries impede the recovery and recrystallization of Ag sheets.
参考文献
| [1] | Lux B.Haupterammlun[M].DGM Villoch,1973 |
| [2] | Harmsen U .[J].Metals,1974,28:683-689. |
| [3] | Osswald E.Z .[J].Metallkund,1935,27:101-105. |
| [4] | Hofrnann W;Kirsch U .[J].Metals,1966,57:305-310. |
| [5] | Raub E.Die Edelmetalle and Ihere Legierungen[M].Springer-verlag,1940 |
| [6] | Yang F;Zhou S;Wang W et al.[J].Journal of Yunnan University,2002,24:354-357. |
| [7] | Yang F;Zhou S;Wang Y et al.Rare metal materials and engineering[J].,2004,33:781-784. |
| [8] | Yang F;Zhou S;Li J et al.Influence of trace manganese additive on propertie of pure silve[J].Precious Metals,2002,23(04):29-32. |
| [9] | He Chunxiao;Ma Guangchen.Phase Diagrams of Precious Metal Alloys[M].,1983 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%