以Na2SO4-K2SO4为熔盐,采用水热均匀沉淀一熔盐煅烧法制备了YAG:Ce33+黄色荧光粉,应用XRD、SEM、荧光分光光度计等测试手段研究了熔盐辅助煅烧对粉体结构、形貌和发光性能的影响.结果表明,以尿素为沉淀剂,采用水热均匀沉淀法制备的前驱体,经Na2SO4-K2SO4熔盐辅助煅烧,900℃时已完全转变为YAG相,与固相法相比,YAG相的完全转变温度降低了600℃,与前躯体直接煅烧相比,YAG相的完全转变温度降低了300℃,荧光粉的发光强度提高了2.4倍.
参考文献
| [1] | Seo SY.;Sohn KS.;Park HD.;Lee S. .Optimization of Gd2O3-based red phosphors using combinatorial chemistry method[J].Journal of the Electrochemical Society,2002(1):H12-H18. |
| [2] | Xu Huarui;Yu Aibing .Synthesis and sintering of tin-doped indium oxide nanoparticals with uniform size[J].Materials Letters,2007,61:4043. |
| [3] | 张克从;张乐惠.晶体化学[M].北京:科学出版社,1981 |
| [4] | Arendt R H;Rosoiowski J H;Szymaszek J W W.Lead zirconate titanate ceramics from molten salt solvent synthesized powders[J].Materials Research Bulletin,1979(14):703. |
| [5] | Tsai Ming-Shyong;Fu Wen-Chuan;Wu Wen-Chang et al.Effect of the aluminum source on the formation of yttrium aluminum garnet (YAG) powder via solid state reaction[J].Journal of Alloys and Compounds,2008,455:461. |
| [6] | Yoon KH.;Kang DH.;Cho YS. .Molten salt synthesis of lead-based relaxors [Review][J].Journal of Materials Science,1998(12):2977-2984. |
| [7] | Jacobs R R et al.Measurement of excited-state-absorption loss for Ce3+ in Y3Al5O12 and implications for tunable 5d-4f rate-earth laser[J].Applied Physics Letters,1978,33:410. |
| [8] | 张太中;张俊英.无机光致发光材料及应用[M].北京:化学工业出版社,2005:108. |
| [9] | 孙家跃;杜海燕;胡文祥.固体发光材料[M].北京:化学工业出版社,2003:161. |
| [10] | 黄燕 .熔盐法制备Y<,2>O<,3>：Eu<'3+>及YAG：Ce<'3+>荧光粉新工艺研究[D].中南大学,2007. |