采用传统固相烧结法制备In2O3掺杂的锆钛酸铅(PZT)铁电陶瓷,研究了In2O3掺杂量对PZT铁电陶瓷材料的相组成、微观结构、介电性能、压电性能及铁电性能的影响.研究结果表明,随着In2O3掺杂量的增加,PZT材料在准同型相界处三方相增加四方相减少,适量掺入In2O3有利于晶粒均匀生长.在不同的铟掺杂剂量下,PZT陶瓷材料分别具有最佳的铁电及压电性能.当铟掺杂量为0.1％(质量分数)时,PZT材料具有最佳的铁电性能,其剩余极化强度为23.43μC/cm2,矫顽场为9.783kV/cm.当铟掺杂量为0.3％(质量分数)时,PZT材料具有最好的压电性能,其tanδ=0.023,d33＝540pC/N,εr=1513,Kp=0.764,Qm=1819.
参考文献
| [1] | 曲远方.功能陶瓷及应用[M].北京:化学工业出版社,2003:327. |
| [2] | Mabud S A .The morphotropic phase boundary in PZTsolid solutions[J].Journal of Applied Crystallography,1980,13(03):211-216. |
| [3] | Xu Yuhuan.Ferroelectric materials and their applications[M].USA:North-Holland,1991:24. |
| [4] | Vasiliu F;Lucuta P Gr;Cibstabtubescu F .Structure-sintering temperature relationship in PZT solid solutions at the morphotropic phase boundary[J].Physical Status Solidi A Applied Research,1983,80(02):637-642. |
| [5] | 张沛霖;钟维烈.铁电材料与器件[M].济南:山东科学出版社,1997:5. |
| [6] | 孙秋,魏兆冬,王福平,姜兆华.Gd掺杂对PZT薄膜介电性能及极化行为的影响[J].无机材料学报,2008(05):872-876. |
| [7] | Chen Yabo;Zhang Yangyang;Jiang Shenglin et al.Studies on white or organic light emitting devices with a single luminescence layer[J].Journal of Function Materials,2008,39(08):379-384. |
| [8] | Gui Zhilun;Li Longtu;Gao Suhua et al.Low temperature sintering of lead-based piezoelectric ceramics[J].Journal of the American Ceramic Society,1989,72(03):486-491. |
| [9] | Corker D L;Whatmore R W;Ringgaard E et al.Liquidphase sintering of PZT ceramics[J].Journal of the European Ceramic Society,2000,20:2039-2045. |
| [10] | 周桃生,黄荣厦,尚勋忠,顾豪爽,郭健勇,柴荔英.掺铟对（Bi0.5Na0.5）0.93Ba0.07TiO3压电陶瓷的影响[J].压电与声光,2008(01):64-66. |
| [11] | 李启寿,肖定全,朱建国.钇掺杂对BSPT高温压电陶瓷铁电性能的影响[J].无机材料学报,2011(02):185-190. |
| [12] | 郑朝丹,张端明,刘心明,刘超军,余春荣,于军.Ti掺杂BiFeO3陶瓷的结构和铁电性能研究[J].无机材料学报,2009(04):745-748. |
| [13] | 贺连星,李承恩.大功率PZT材料锰掺杂改性研究[J].功能材料,2000(05):525-527. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%