以分析纯V2O5粉体为原料、H2O2为溶剂，采用电磁-超声波搅拌方式的无机溶剂-凝胶工艺，在ITO导电玻璃衬底上制备了V2O5薄膜；并研究了热处理温度对其形貌和结构的影响。结果表明：室温下V2O5薄膜为非晶无定形结构，400℃热处理后，薄膜中出现了β-V2O5相，450℃热处理后基本上全为β-V2O5相，500℃热处理后又出现了α-V2O5相；薄膜在350～400℃热处理后，表面较平滑、均匀，出现颗粒；450℃热处理后主要由瓣状、片状及短棒状多晶堆积而成；500℃热处理后主要由棒状多晶组成。
Use V2O5 powders as raw materials and H2O2 as solvent, V2O5thin films were prepared on ITO conducting glass substrates by electromagnetism-ultrasonic-stirred inorganic sol-gel technology. The influence of the heat treatment temperature on the morphology and structure of V2O5 thin films was studied. The results show that the V205 thin film was amorphous structure crystal at room temperature, β-V2O5 phase appeared after heat treatment at 400℃, all were β-V2O5 phase when the heat treatment temperature was 450℃, and the α-V205 appeared again after 500 ℃. The surface of the thin film was smooth and homogeneous, and particles appeared after heat treatment at 350--400℃. The surface morphology after 450℃ were piled up by petaloid, sheet and short- elavate polycrystal, and which was made up by clavate polyerystal after 500℃.
参考文献
| [1] | S.Albonetti;G.Baldi;A.Barzanti .Chlorinated organics total oxidation over V2O5/TiO2 catalysts prepared by polyol-mediated synthesis[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2007(2):309-315. |
| [2] | Sahana MB;Sudakar C;Thapa C;Lawes G;Naik VM;Baird RJ;Auner GW;Naik R;Padmanabhan KR .Electrochemical propertiesOf V2O5 thin films deposited by spin coating[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2007(1/3):42-50. |
| [3] | 李莉,童茂松,翁爱华.V2O5薄膜在传感器上的研究进展[J].功能材料,2005(10):1482-1484,1488. |
| [4] | Jolanta Swiatowska-Mrowiecka;Vincent Maurice;Sandrine Zanna;Lorena Klein;Philippe Marcus .XPS study of Li ion intercalation in V{sub}2O{sub}5 thin films prepared by thermal oxidation of vanadium metal[J].Electrochimica Acta,2007(18):5644-5653. |
| [5] | P. Balog;D. Orosel;Z. Cancarevic .V_2O_5 phase diagram revisited at high pressures and high temperatures[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):87-98. |
| [6] | Ozer N. .ELECTROCHEMICAL PROPERTIES OF SOL-GEL DEPOSITED VANADIUM PENTOXIDE FILMS[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1997(1/2):80-87. |
| [7] | 黄春明 .TiO<,2>：Co和VO<,x>纳米材料的制备及其特性研究[D].兰州大学,2007. |
| [8] | 周海佳 .VO<,x>纳米材料的水热合成与电泳沉积研究[D].兰州大学,2008. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%