简述硫印、热酸蚀、电解腐蚀、冷酸蚀和枝晶腐蚀5种低倍检验方法,其中枝晶腐蚀低倍检验方法,能够清晰地显示连铸坯的凝固组织和缺陷,该方法是研究连铸坯缺陷,提高钢材质量的最佳选择方法。并通过不同检验方法对比图例来证明枝晶腐蚀低倍检验方法的优越性。
5 macroscopic examination methods of sulphur print,hot etching,electrolytic acid cleaning etching,cold etching and dendrite corrosion were summarized.Dendritical etching is able to illustrate clearly the solidification structures and its defects of casting slabs.It is the best choice to study the slab defect and improve slab quality.The advantage of dendrite corrosion is proved by comparing the testing illustrations with different methods.
参考文献
| [1] | 许庆太;王文仲.连铸钢坯低倍检验和缺陷图谱[M].北京:中国标准出版社,2009:1. |
| [2] | 李靖,喻承欢,李凤喜,徐静波,邱同榜,柳志敏,吴永生.冷蚀检验在连铸坯质量控制中的应用实践[J].炼钢,2003(02):13-16,20. |
| [3] | 王英.连铸方坯低倍组织及缺陷特性分析[J].江苏冶金,2003(06):35-37. |
| [4] | 顾然;于秉芳.连铸板坯中硫化物夹杂的调查研究[J].河北矿冶学院学报,1982(01):8. |
| [5] | 史宸兴.连铸钢坯质量[M].北京:冶金工业出版社,1980:27. |
| [6] | 刘国贵,何宇明,余挺进.小方坯连铸电磁搅拌工艺参数优化实践[J].连铸,2004(04):11-13. |
| [7] | 陈永.连铸结晶器电磁搅拌技术[J].钢铁钒钛,2003(02):29-33. |
| [8] | 胡坤太,仇圣桃,张慧,干勇,周宏,欧建军,朱斌,何宇明.重钢小方坯连铸机内置式结晶器电磁搅拌器的研制[J].钢铁,2003(05):22-24. |
| [9] | 阎朝红,徐国栋.3#宽厚板坯连铸机凝固末端轻压下技术[J].宝钢技术,2008(04):63-67. |
| [10] | 宋景欣,朱苗勇,祭程,程乃良.板坯连铸动态轻压下模型的开发与应用[J].中国冶金,2009(07):23-27,32. |
| [11] | 李平,薛庆国,关勇,王静松,唐雪峰,许刚,丁丽华,赵志刚.电脉冲孕育处理对方坯连铸09CuPCrNi钢凝固组织的影响[J].北京科技大学学报,2004(02):219-221. |
| [12] | 李平,关勇,于功利,孟劲松,唐雪峰,王阿鼎.电脉冲孕育处理改善连铸坯凝固组织的试验研究[C].2005中国钢铁年会论文集,2005:384-388. |
| [13] | 李平,关勇,唐雪峰,王阿鼎,丁丽华.电脉冲处理钢液改善铸坯凝固组织的工业化试验[J].过程工程学报,2006(z1):57-61. |
| [14] | 冯军,陈伟庆,韩静,段贵生.连铸参数对高碳钢小方坯二次枝晶间距的影响[J].钢铁,2006(09):37-39,43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%