采用溶胶-凝胶浸渍提拉法分别在氧化硅和石英衬底上制备TiO2薄膜,并以不同的退火温度保温30min。通过采用X射线衍射仪（XRD）、扫描电镜（SEM）及紫外-可见分光光度计,对TiO2薄膜的结构和光学性能进行了详细分析,并且进行了对甲基橙的降解实验。研究结果表明,随着退火温度的升高,薄膜的晶相由锐钛矿向金红石转变,转变温度在700～800℃之间。在该转变过程中,薄膜结晶程度良好,800℃时薄膜表面平整无开裂;随着热处理温度的升高,TiO2薄膜的吸收峰蓝移,紫外区吸收范围扩大。在800℃退火时,薄膜中所含锐钛矿TiO2为31.4%（质量分数）。此时薄膜表现出最高的甲基橙降解率。
Titanium dioxide films were prepared on silica and quartz substrates by sol-gel dip-coating.These films were subsequently thermally annealed at temperatures for 30min;the structural and optical properties of prepared titanium dioxide films were analysed by X-ray diffraction(XRD),scanning electron microscopy(SEM) and UV-visible spectrophotometer,respectively.The ability to degrade methyl orange of these films was also studied.We found that the crystalline phase of the changed gradually from anatase to rutile as annealing temperature increased,and this transition took place at temperatures ranging from 700 to 800℃.During the transition,titanium dioxide films exhibited good,and no cracks were found even after annealing at 800℃.As annealing temperature increased,the absorption peak of titanium dioxide films had a blue-shifted,resulting in the expansion of absorption range in UV area.Titanium dioxide film prepared by this method and annealed at 800℃ for 30min which contained 31.4wt% anatase showed the highest degradation ratio of methyl orange.
参考文献
| [1] | Fujishima A;Honda K .Photocatalysis of water at a semiconductor electrode[J].Nature,1972,238:37-38. |
| [2] | Frank S N;Bard A J .Heterogeneous photocatalytic oxidation of cyanide and sulfite in aqueous solutions at semiconductor powders[J].Journal of Physical Chemistry,1977,81:14841489. |
| [3] | 杨小儒,郭震宁,李君仁,刘明强.纳米二氧化钛薄膜的制备及光致发光研究[J].功能材料,2007(06):1016-1018,1026. |
| [4] | Bacsa R R;Kiwi J .Effect of rutile phase on the photocat alytic properties of nanocrystalline titania during the deg radation of p-coumaric acid[J].Applied Catalysis B:Environmental,1998,16:19-29. |
| [5] | 杨南如.无机非金属材料测试方法[M].武汉:武汉理工大学出版社,1990:156-176. |
| [6] | Jung HS;Lee JK;Lee J;Kang BS;Jia Q;Nastasi M;Noh JH;Cho CM;Yoon SH .Mobility enhanced photoactivity in sol-gel grown epitaxial anatase TiO2 films[J].Langmuir: The ACS Journal of Surfaces and Colloids,2008(6):2695-2698. |
| [7] | Jung HS;Lee JK;Lee J;Kang BS;Jia Q;Nastasi M .Strain relaxation in sol-gel grown epitaxial anatase thin films[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2008(11):4205-4208. |
| [8] | 张瑜,梁伟,云洁,白爱英,薛晋波.Pt对TiO2薄膜的结构及可见光光催化活性的影响[J].功能材料,2009(03):508-511. |
| [9] | 张鹏会;孔爱平;韩迪.TiO2光催化降解有机污染物研究进展[J].甘肃石油和化工,2009(02):4-5. |
| [10] | Wong C C;Chu W .The direct photolysis and photocatalytic degradation of alachlor at different TiO2 and UV sources[J].Chemosphere,2003,50(08):981-987. |
| [11] | Tusnelda E. Doll;Fritz H. Frimmel .Kinetic study of photocatalytic degradation of carbamazepine, clofibric acid, iomeprol and iopromide assisted by different TiO_2 materials—determination of intermediates and reaction pathways[J].Water research: A journal of the international water association,2004(4):955-964. |
| [12] | 秦友兰;冯斌;王银峰 .光纤TiO2薄膜的制备及理化特性研究[J].化工新型材料,2002,33(02):205. |
| [13] | 田雨,吴岳英.溶胶-凝胶法合成二氧化钛粉末的工艺条件优化[J].化学工程师,2004(11):9-11. |
| [14] | Gao S H;Gao L H;Zhou K S.Study on photocatalytic activity of Ni^2+ doped TiO2 thin films[A].Piscataway,2010:1-3. |
| [15] | Jing Zhang;Qian Xu;Zhaochi Feng .Importance of the Relationship between Surface Phases and Photocatalytic Activity of TiO2[J].Angewandte Chemie,2008(9):1766-1769. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%