为了提高GH907合金的抗高温和抗热腐蚀性能,利用低压等离子喷涂技术在其表面制备了NiCoCrAlY 粘接层和NiCr粘接层,并对2种粘接层的抗热震性能进行了研究.结果表明,NiCoCrAIY粘接层和NiCr粘接层经过10次热震后,表面都有裂纹产生,且NiCoCrAlY粘接层的裂纹较NiCr粘接层的粗大;在横截面上NiCr粘接层只有沿喷涂颗粒断裂的垂直裂纹,而NiCoCrAlY粘接层不仅有垂直裂纹,还存在沿界面扩展的横向裂纹;NiCr粘接层的抗热震性能相比NiCoCrAlY粘接层的更好一些.
参考文献
| [1] | 马天军,赵玉才,郁雷芸.低膨胀GH907合金700℃长期时效后的性能[J].钢铁研究学报,2003(z1):107-110. |
| [2] | Kawasaki A;Watanabe R .Thermal fracture behavior of metal/ceramic functionally graded material[J].Engineering Fracture Mechanics,2002,69:1713-1728. |
| [3] | Khan AN.;Lu J. .Behavior of air plasma sprayed thermal barrier coatings, subject to intense thermal cycling[J].Surface & Coatings Technology,2003(1):37-43. |
| [4] | Getsov L B;Rybnikov A I;Krukovski P G .Behaviour prediction of covering coatings under long-duration opration conditons[J].Material at High Temperature,1995,13(02):99-101. |
| [5] | Tsai H L;Tsai P C .Thermal cyclic response of laser-glazed plass-sprayed ZrO2-19.5 %Y2O3/Ni-22Cr-10Al-Y thermal barrier coatings[J].Material Science and Engieering,1994,A177:227-230. |
| [6] | 工程材料手册编辑委员会.工程材料实用手册[M].北京:中国标准出版社,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%