钢轨钢的接触疲劳一直为铁路运输部门和研究机构所重视.轮-轨经过长时间滚动接触会导致轨面剥落,产生疲劳.本文综述了钢轨钢的滚动接触疲劳特征及其成因,探讨了提高钢轨钢接触疲劳寿命的途径.
参考文献
| [1] | 徐罗平;蒋克;徐莉 等.进口钢轨核伤原因分析[J].理化检验-物理分册,1997,33(04):35-36. |
| [2] | Hans M;Herbert S;Klaus W-Rail Rolling Contact Fatigue .The Performance of Naturally Hard and Head-Hardened Rails in Track[J].Wear,1996,191:54-64. |
| [3] | Sugino K;Kageyama H;Urashima C .Metallurgical Improvement of Rail for the Reduction of Rail-Wheel Fatigue Failures[J].Wear,1991,144:319-328. |
| [4] | Cannon D F;Pradier H .Rail Rolling Contact Fatigue Research by the European Rail Research Institute[J].Wear,1996,191:1-13. |
| [5] | 朱敦伦;朱法义;黄善钧 .齿轮接触疲劳破坏机理研究[J].哈尔滨工业大学学报,1979,11(01):143-152. |
| [6] | 卢观健;杨克;袁龙英 .淬火钢轨的损伤与失效分析[J].中国铁道科学,1994,15(01):36-51. |
| [7] | Su X;Clayton P .Surface-Initiated Rolling Contact Fatigue of Pearlitic and Low Carbon Bainitic Steels[J].Wear,1996,197:137-144. |
| [8] | 戴利民 .U71Mn钢不同组织接触疲劳性能的试验研究[D].北京:铁道部科学研究院,1984. |
| [9] | Beynon J H;Garnham J E;Sawley K J .Rolling Contact Fatigue of Three Pearlitic Rail Steels[J].Wear,1996,192:94-111. |
| [10] | Clayton P .Tribological Aspects of Wheel-Rail Contact:AReview of Recent Experimental Research[J].Wear,1996,191:170-183. |
| [11] | Baumann G;Fecht H J;Liebelt S .Formation of White-Etching Layers on Rail Treads[J].Wear,1996,191:133-140. |
| [12] | Yang Y Y;Fang H S;Zheng Y K et al.The Failure Models Induced by White Layers during Impact Wear[J].Wear,1995,185:17-22. |
| [13] | Newcomb S B;Stobbs W M .A Transmission Electron Microscopy Study of the White-Etching Layer on a Rail Head[J].Materials Science and Engineering,1984,66(02):195-204. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%