通过采用不同的润滑条件、压下率、退火温度，研究了DC03冷轧微碳钢冷轧和退火过程沿钢板厚度方向织构的形成和演变机制，结果表明冷轧时使用全润滑轧制，当压下率为75%，退火温度为750 ℃时，可得到最佳的r值。
Formation and evolution mechanism of texture of DC03 cold-rolling micron-carbon steel along thickness are studied during cold-rolling and annealing under different lubrication conditions, reduction radios and annealing temperatures. The results show that the best r value can be obtained when completely lubricated rolling is used during cold-rolling, the reduction radio is 75%, and annealing temperature is 750 ℃.