以电阻率为性能指标,采用正交试验对化学镀Ni-W-P的镀液配方进行优化,得到最优配方与工艺为:NiSO4·6H2O 15 g/L,NaH2PO2·H2O 25 g/L,Na2WO4·2H2O 10g/L,Na3C6H5O7·2H2O60 g/L,C3H6O3 5 mL/L,NH4C1 30g/L,pH=9,温度88℃,时间2h.采用扫描电镜、X射线衍射仪、显微硬度计等研究了Ni-W-P合金镀层的表面形貌、结构、显微硬度等性能.在最佳配方与工艺下,化学镀Ni-W-P的镀速为6.9 μm/h,所得Ni-W-P合金镀层的电阻率为204.7 mΩ·cm,为典型的非晶态结构,表面均匀分布着大小不一、致密的胞状结构,镀层与基体之间结合力牢固,显微硬度高于Ni-P镀层,耐磨性和耐蚀性均优于Ni-P镀层.
参考文献
| [1] | 姜晓霞;沈伟.化学镀理论及实践[M].北京:国防工业出版社,2000:87-90. |
| [2] | 许晓丽,黄燕滨,张平,孟昭福,梁志杰,刘德刚,刘波.化学镀Ni-W-P镀液及工艺优化研究[J].电镀与涂饰,2005(02):18-20. |
| [3] | Y. Gao;Z.J. Zheng;M. Zhu .Corrosion resistance of electrolessly deposited Ni-P and Ni-W-P alloys with various structures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):98-103. |
| [4] | E.Valova;S.Armyanov;A.Franquet;A.Hubin;O.Steenhaut;J.-L.Delplancke;J.Vereecken .Electroless deposited Ni-Re-P, Ni-W-P and Ni-Re-W-P alloys[J].Journal of Applied Electrochemistry,2001(12):1367-1372. |
| [5] | HU Y J;XIONG L;MENG J L .Electron microscopic study on interfacial characterization of electroless Ni-W-P plating on aluminum alloy[J].Applied Surface Science,2007,253(11):5029-5034. |
| [6] | 崔培英.玻璃表面化学镀Co-Ni-P合金的研究[J].山东化工,2008(11):4-6. |
| [7] | HUANG Ying,HUANG Fei,ZHAO Wentao,SHI Ke,ZHAO Li,WANG Yanli.The study of electroless Ni-W-P alloy plating on glass fibers[J].稀有金属(英文版),2007(04):365-371. |
| [8] | 宗云,郭荣新,何冰清,刘宏.不同镀液组分对化学沉积Ni-W-P合金层组织和性能的影响[J].表面技术,2009(06):9-12. |
| [9] | 姚怀,苌清华,王喜然,陈艳芳.镀液pH值对铝合金化学镀Ni-W-P三元合金镀层组织和性能的影响[J].轻合金加工技术,2010(07):45-48. |
| [10] | 陈秉玉,王连金,程先安.Fe-Cr-Al/Si非晶态薄膜的电阻-应力特性[J].航空学报,1991(08):411. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%