为了实现工业纯钛TA1的数值模拟,制定合理的自由锻工艺参数,利用Gleeble-1500D热模拟实验机对工业纯钛TA1在变形温度为700、800、900和950℃和应变速率为0.01、0.1、1和5 s-1条件下的流变应力行为进行研究,最大变形程度为真应变0.7.结果表明:工业纯钛TA1在热压缩变形过程中,出现了动态回复与再结晶;流变应力随温度的升高而降低,随变形速率的减小而降低;在高的变形温度与低的应变速率下,工业纯钛TA1容易出现软化;求得了热变形激活能(Q)和双曲正弦形式的Arrhenius本构方程.
参考文献
| [1] | Boyer R R .An overview on the use of titanium in the aerospace industry[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,1996,213(01):103-l14. |
| [2] | D.R.Chichili;K.T.Ramesh;K.J.Hemker .The high-strain-rate response of alpha- titanium: experiments, deformation mechanisms and modeling[J].Acta materialia,1998(3):1025-1043. |
| [3] | S. NEMAT-NASSER;W. G. GUO;J. Y. CHENG .MECHANICAL PROPERTIES AND DEFORMATION MECHANISMS OF A COMMERCIALLY PURE TITANIUM[J].Acta materialia,1999(13):3705-3720. |
| [4] | 周伟,杨英丽,于振涛,周廉.工业纯钛TA2的高温变形机制研究[J].稀有金属,2003(06):721-725. |
| [5] | Zeng, ZP;Jonsson, S;Zhang, YS .Constitutive equations for pure titanium at elevated temperatures[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2009(1/2):116-119. |
| [6] | 刘晓燕,赵西成,杨西荣,王成.120°模具室温ECAP制备工业纯钛的热压缩变形行为[J].稀有金属材料与工程,2012(04):667-671. |
| [7] | 刘晓燕,赵西成,杨西荣,王成.120°模具室温ECAP制备工业纯钛的压缩变形本构关系[J].中国有色金属学报（英文版）,2012(05):1292-1297. |
| [8] | 崔忠圻;覃耀春.金属学与热处理[M].北京:机械工业出版社,2007 |
| [9] | 周计明,齐乐华,陈国定.热成形中金属本构关系建模方法综述[J].机械科学与技术,2005(02):212-216. |
| [10] | 李德君,刘平,董企铭,田保红,任凤章.Mg-3Al-1Zn-0.8Nd合金热压缩变形流变应力的研究[J].材料热处理学报,2008(05):26-30. |
| [11] | 李伟,高家诚.Mg-6.5Y-2.5Nd-0.6Zr合金热压缩变形流变应力行为[J].材料热处理学报,2011(03):40-46. |
| [12] | 王俊峰,贾淑果,陈少华,宋克兴,谢秋风,刘平.变形量对Cu-Ni-Si合金再结晶行为的影响[J].河南科技大学学报（自然科学版）,2012(01):5-7,11. |
| [13] | 王立民,张红,吕成林,邰青安,王照坤,杨钢,刘正东.0Cr11Ni2MoVNb钢高温压缩变形的流变应力[J].金属热处理,2008(10):74-76. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%