利用3种二胺单体1,4-双(4-氨基-2-三氟甲基苯氧基)苯、4,4’-双(4-氨基-2-三氟甲基苯氧基)二苯醚和4,4’-双(4-氨基-2-三氟甲基苯氧基)六氟丙烷分别与3种二酐单体1,2,3,4-环丁烷四酸二酐(CBDA)、均苯四甲酸二酐(PMDA)和3,3’,4,4’-二苯醚四酸二酐(ODPA)进行低温溶液缩聚反应,再经热酰亚胺化制备出9种聚酰亚胺(PI)薄膜.结果表明,这些PI具有较好的溶解性,可溶解于氨型强极性溶剂,在弱极性溶剂中也有一定的溶解性；CBDA和ODPA基PI在450 nm处的透光率超过80％,且CBDA基PI的紫外截止波长为310 nm,更接近无色,但其热稳定性最差,5％热分解温度在420℃左右,而PMDA和ODPA基PI的热稳定性较好.
参考文献
| [1] | Matsumoto T;Kawabata S;Takahashi R .Alicyclic polyimides based on bicyclo[2.2.1]heptane2,3,5,6-tetracarboxylic 2,3;5,6-dianhydrides[J].High performance polymers,2006(5):719-726. |
| [2] | Liu JG;Nakamura Y;Suzuki Y;Shibasaki Y;Ando S;Ueda M .Highly refractive and transparent polyimides derived from 4,4'-[m-sulfonylbis(phenylenesulfanyl)]diphthalic anhydride and various sulfur-containing aromatic diamines[J].Macromolecules,2007(22):7902-7909. |
| [3] | Barnali Dasgupta;Suman Kumar Sen;Samarendra Maji;Shyambo Chatterjee;Susanta Banerjee .Synthesis and Characterization of Highly Soluble Poly(ether imide)s Containing Indane Moieties in the Main Chain[J].Journal of Applied Polymer Science,2009(6):3640-3651. |
| [4] | Yang CP.;Chen RS.;Chen KH. .Effects of diamines and their fluorinated groups on the color lightness and preparation of organosoluble aromatic polyimides from 2,2-bis[4-(4-amino-2-trifluoromethylphenoxy) phenyl]-hexafluoropropane[J].Journal of Polymer Science, Part A. Polymer Chemistry,2003(7):922-938. |
| [5] | Yang CP;Hsiao SH;Chen YC .Soluble and light-colored polyimides from 2,3,2 ',3 '-oxydiphthalic anhydride and aromatic diamines[J].Journal of Applied Polymer Science,2005(3):1352-1360. |
| [6] | Chung, CL;Lee, WF;Lin, CH;Hsio, SH .Highly Soluble Fluorinated Polyimides Based on an Asymmetric Bis(ether amine): 1,7-Bis(4-amino-2-trifluoromethylphenoxy)naphthalene[J].Journal of Polymer Science, Part A. Polymer Chemistry,2009(7):1756-1770. |
| [7] | Jang W;Shin D;Choi S;Park S;Han H .Effects of internal linkage groups of fluorinated diamine on the optical and dielectric properties of polyimide thin films[J].Polymer: The International Journal for the Science and Technology of Polymers,2007(7):2130-2143. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%