以Al(NO3)3·9H2O、Y(NO3)3·6H2O和Nd2O3为原料,采用硝酸盐热分解法在1000 ℃左右合成了单相Nd:YAG陶瓷超细粉体.采用XRD及SEM等测试手段对Nd:YAG陶瓷材料进行了表征.结果表明,当焙烧温度为1000 ℃时,前驱粉体可以直接得到YAG立方晶相,没有YAM和YAP等中间相生成,煅烧所得的粉末颗粒细小均匀,呈椭球状,分散性较好,粒径在150～200 nm之间.使用0.5%(质量分数,下同)的正硅酸乙酯作为烧结添加剂,前驱粉体经1700 ℃真空热压烧结5 h后得到具有一定透明度的Nd:YAG多晶陶瓷,晶粒大多在3～4 μm之间,晶界间还分布着少量的气孔.
参考文献
| [1] | With G D;Vandifh H J .[J].MaterRes Bull,1984,19(02):1669. |
| [2] | Akio Ikesue;Iso Furusato;Kiichiro Kamata .[J].Journal of the American Ceramic Society,1995,78(01):225. |
| [3] | Ikesue Akio;Kinshita Toshiyuki;Kamata Kiichiro .[J].Journal of the American Ceramic Society,1995,78(04):1033. |
| [4] | Zhou Y H;Lin J .[J].Optical Materials,2002,20:13. |
| [5] | Gowda G .[J].JMater Sci Lett,1986,5:1029. |
| [6] | Matsubara I;Paranthaman M .[J].Materials Research Bulletin,2000,35:217. |
| [7] | Li Jiguang;Ikegami Takayasu;Lee Jongheun .[J].Journal of the American Ceramic Society,2000,83(04):961. |
| [8] | Masashi Inoue;Hiroyuki Otsu;Hiroshi Kominami et al.[J].Journal of the American Ceramic Society,1991,74:1452. |
| [9] | Shea L E;Mckittriek J;lopez o A et al.[J].Journal of the American Ceramic Society,1996,79(12):3257. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%