综述了镁合金的塑性成形工艺性能、镁合金丝成形工艺方法的研究现状和镁合金丝成形工艺的发展趋势.形变温度、载荷形式和晶粒尺寸对镁合金的塑性变形能力影响很大;通过升高温度和使镁合金处于三向压应力状态可以显著提高镁合金的塑性,因此热挤压是一种可行的镁合金丝塑性成形方法;拉拔成形过程中的应力状态对镁合金的塑性发挥不利,但在锾合金丝拉拔过程中引入电磁场、电脉冲等外场可以使镁合金的温度快速升高、晶粒细化,从而大幅提高镁合金的塑性,外场作用下生产效率极高的拉拔成形新技术是未来镁合金丝成形工艺的研究与发展方向.
参考文献
| [1] | 丁文江;袁广银;曾小勤.镁合金科学与技术[M].北京:科学出版社,2007:24. |
| [2] | Schumann S;Friedrich H .Current and future use of magnesium in the automobile industry[J].Materials Science Forum,2003,419-422:433. |
| [3] | Yo Kojima .Platform science and technology for advanced magnesium alloys[J].Materials Science Forum,2000,350-351:3. |
| [4] | Mordike B L;Ebert T .Magnesium:Properties-application-potential[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2001,302:37. |
| [5] | Rinotino G;Lussana D;Massazza M et al.Structure evolution of EV31 Mg alloy[J].Journal of Alloys and Compounds,2008,463:200. |
| [6] | 张津;章宗和;汤明波.镁合金及应用[M].北京:化学工业出版社,2004:283. |
| [7] | 余琨,黎文献,王日初,马正青.变形镁合金的研究、开发及应用[J].中国有色金属学报,2003(02):277-288. |
| [8] | Colleen J. Settles;Mark A. Gibson .Current Wrought Magnesium Alloys: Strengths and Weaknesses[J].JOM,2005(5):46-49. |
| [9] | 陈维平,詹美燕,陈宛德,张大童,李元元.变形镁合金的塑性加工技术研究及展望[J].特种铸造及有色合金,2007(01):40-43. |
| [10] | 张丁非,刘杰慧,胡红军,谭小明.高性能变形镁合金SPD挤压技术的研究进展[J].热加工工艺,2009(11):102-105. |
| [11] | 王艳丽,郭学锋,黄丹,王英.高性能变形镁合金研究进展及应用[J].热加工工艺,2011(18):11-14. |
| [12] | 田昊洋,唐国翌,丁飞.高能电脉冲处理对镁合金丝材性能的影响[J].有色金属,2008(04):1-4. |
| [13] | 吕涛 .Mg-Al共晶和AZ91D镁合金焊丝的制备、组织、性能及焊接试验[D].西安理工大学,2007. |
| [14] | 吴婕,吴凤鸣.新型口腔生物医用材料--镁及镁合金[J].口腔医学,2007(03):159-161. |
| [15] | Di Mario C;Griffiths H;Goktekin O;Peeters N;Verbist J;Bosiers M;Deloose K;Heublein B;Rohde R;Kasese V;Ilsley C;Erbel R .Drug-eluting bioabsorbable magnesium stent.[J].Journal of interventional cardiology,2004(6):391-395. |
| [16] | Zartner P;Cesnjevar R;Singer H;Weyand M .First successful implantation of a biodegradable metal stent into the left pulmonary artery of a preterm baby.[J].Catheterization and cardiovascular interventions: Official journal of the Society for Cardiac Angiography & Interventions,2005(4):590-594. |
| [17] | Lu S K;Yeh H I;Tian T Y et al.Degradation of magnesium alloys in biological solution and reduced phenotypic expression of endothelial cell grown on theses alloys[J].IFMBE Proceedings,2007,15:98. |
| [18] | Ron Waksman;Rajbabu Pakala;Parmod K Kuchulakanti et al.Safety and efficacy of bioabsorbable magnesium alloy scents in porcine coronary arteries[J].Catheteriz Cardiov Interv,2006,68:607. |
| [19] | Colin J McMahon;Paul Oslizlok et al.Early restenosis following biodegardable stent implantation in an aoaopulmonary collateral of a patient with pulmonary atresia and hypoplastic pulmonary arteries[J].Catheterz Cardiov Interv,2007,69:735. |
| [20] | Cahn RW;丁道云.非铁合金的结构与性能[M].北京:科学出版社,1999 |
| [21] | Agnew S R;Yoo M H;Tome C N .Application of texture simulation to understanding mechanical behavior of Mg and solid solution alloys containing Li or Y[J].ACTA MATERIALIA,2001,49:4277. |
| [22] | Agnew S R;Tome C N;Brown D W et al.Study of slip mechanisms in a magnesium alloy by neutron diffraction and modeling[J].Sripta Mater,2003,48:1003. |
| [23] | 刘正;张奎;曾小勤.镁基轻质合金理论基础及其应用[M].北京:机械工业出版社,2002 |
| [24] | 任红霞,刘长瑞,张娟,鞠克江.改善变形镁合金塑性的研究进展[J].新技术新工艺,2008(07):79-82. |
| [25] | 黄光胜,黄光杰,汪凌云,潘复生.变形镁合金塑性的改善[J].材料导报,2006(01):39-41. |
| [26] | 金文中,刘顺华,刘黎明,刘斌,胡晓菊,董长富.镁合金焊丝的成形工艺及组织性能研究[J].金属成形工艺,2003(06):73-75,82. |
| [27] | 马胜强 .小直径镁合金丝材的制备工艺、组织及性能研究[D].西安理工大学,2008. |
| [28] | 徐春杰,郭学锋,张忠明,贾树卓,刘礼.往复挤压及正挤压AZ91D镁合金丝材的组织及性能[J].稀有金属材料与工程,2007(03):500-504. |
| [29] | 郭学锋,任昉 |
| [30] | 郭学锋,任昉.高强度Mg-Zn-Y-Ce-Zr合金细丝的制备与表征[J].中国有色金属学报,2011(02):290-295. |
| [31] | 李强 .镁合金温静液挤压工艺试验及仿真研究[D].哈尔滨工业大学,2007. |
| [32] | 金文中,刘顺华.镁合金焊丝的热挤压-拉拔工艺及其变形机理[J].材料科学与工艺,2005(05):466-469. |
| [33] | 田昊洋,唐国翌,丁飞,徐卓辉,姜雁斌.镁合金丝材的电致塑性拉拔研究[J].有色金属,2007(02):10-13. |
| [34] | 徐奔 .AZ31镁合金丝材拉拔工艺的研究[D].哈尔滨工业大学,2006. |
| [35] | 晁红颍 .AZ31镁合金超细丝的冷拉拔及退火工艺研究[D].哈尔滨工业大学,2007. |
| [36] | 王冰 .热挤压法制备镁合金焊丝及其焊接接头分析[D].西安理工大学,2007. |
| [37] | 陈振华.变形镁合金[M].北京:化学工业出版社,2005:1. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%