以Ti为基体,通过热分解Pb(NO3)2水溶液制备了Ti/PbO2电极以及含有SnO2+Sb2O3中间层的Ti/SnO2+Sb2O3/PbO2电极,并将所制备的电极应用于模拟苯酚废水的电化学氧化降解.结果表明:含有SnO2+Sb2O3中间层的Ti/SnO2+Sb2O3/PbO2电极在相同的操作电流密度下,槽电压低于未加中间层的Ti/PbO2电极.以聚合前驱体制得的Ti/SnO2+Sb2O3/PbO2电极为阳极时,在25℃,电流密度15 mA/cm2下,恒电流电解浓度为2.13×10-3mol/L的模拟苯酚废水,电解3.0 h后,苯酚浓度降为1.67×10～mol/L,苯酚去除率达99.2%;电解6.5 h后,COD下降率为84.3%.阳极寿命快速检测实验结果表明,添加锡锑中间层后的Ti/SnO2+Sb2O3/PbO2电极,其寿命显著提高.
参考文献
| [1] | Panizza M.;Cerisola G.;Bocca C. .Electrochemical treatment of wastewater containing polyaromatic organic pollutants[J].Water research: A journal of the international water association,2000(9):2601-2605. |
| [2] | Rajkumar D et al.[J].Journal of Hazardous Materials,2004,113(1-3):123. |
| [3] | Szpyrkowics L et al.[J].Water Research,2005,39(08):1601. |
| [4] | 冯玉杰,沈宏,崔玉虹,刘峻峰.钛基二氧化铅电催化电极的制备及电催化性能研究[J].分子催化,2002(03):181-186. |
| [5] | Kim KW.;Savinell RF.;Kuppuswamy M. .Electrochemical oxidation of benzene at a glassy carbon electrode[J].Journal of Applied Electrochemistry,2000(5):543-549. |
| [6] | 王雅琼,童宏扬,许文林.不同前驱体制备的锡锑中间层对Ti/SnO2+Sb2O3/PbO2电极性能的影响[J].稀有金属材料与工程,2004(09):976-979. |
| [7] | Feng Y J;Li X Y .[J].Water Research,2003,37(10):2399. |
| [8] | Quiroz M A et al.[J].Applied Catalysis B:Environmental,2005,59(3-4):259. |
| [9] | 王雅琼,童宏扬,许文林.热分解法制备的Ti/SnO2+Sb2O3/PbO2电极性质研究[J].无机材料学报,2003(05):1033-1038. |
| [10] | 赵国华,周兵,朱仲良.苯酚溶液电解降解的过程分析及中间体的研究[J].同济大学学报(自然科学版),2000(05):597-599,625. |
| [11] | Comninellis Ch et al.[J].Journal of Applied Electrochemistry,1991,21(08):703. |
| [12] | Kotz R et al.[J].Journal of Applied Electrochemistry,1991,21(01):14. |
| [13] | Kakihana M .[J].Journal of Sol-Gel Science and Technology,1996,6:7. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%