用高纯氩气保护的室温球磨技术制备了FeSiAl纳米晶合金粉末;用XRD对原料粉末的合金化过程及合金粉末粒径和微观应变随球磨时间的变化进行了研究;用SEM、DSC对制得的FeSiAl纳米晶合金粉末的显微形貌及固态相变进行了研究.结果表明:在球磨初始的冷焊阶段,硅、铝原子就已经进入铁的晶格形成间隙固溶体,随着球磨时间的增加合金粉末微观应变增加、平均粒径迅速减小,球磨40 h后获得的合金粉末的平均粒径达到9 nm左右;球磨过程中形成的大量晶格畸变、微观应变等因素降低了合金粉末的相变温度,并使合金粉末处于不稳定能态.
参考文献
| [1] | S. Sarkar;C. Bansal .Atomic disorder-order phase transformation in nanocrystalline Fe-Al[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):135-142. |
| [2] | GUG-HAO CHEN;C. SURYANARAYANA;F.H. (SAM) FROES .Structure of Mechanically Alloyed Ti-Al-Nb Powders[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1995(6):1379-1387. |
| [3] | B. Zuo;N. Saraswati;T. Sritharan;H.H. Hng .Production and annealing of nanocrystalline Fe-Si and Fe-Si-Al alloy powders[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):210-216. |
| [4] | 李小强,胡连喜,王尔德.机械球磨对Ti/Al混合粉末组织和热稳定性影响的研究[J].材料科学与工艺,2002(01):14-18. |
| [5] | 程军胜,郝斌,陈汉宾,杨滨,樊建中,张济山.低温球磨制备纳米晶Al-Zn-Mg-Cu合金粉末的热稳定性研究[J].金属热处理,2006(12):19-24. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%