采用多壁碳纳米管(MWCNTs)和片状石墨(FNG)的复合物作导电剂来改善LiCoO2电极的电化学性能,并用恒电流充放电和扫描电子显微镜(SEM)对这种含MWCNTs的LiCoO2电极进行了研究.结果表明,复合物导电剂提高了LiCoO2电极的电化学性能.MWCNTs/FNG质量比为5的复合物(FNGMWCNTs)作导电剂,LiCoO2电极的0.2C首次放电容量约为154.2mAh/g.和单纯的MWCNTs作导电剂相比,FNGMWCNTs作导电剂,LiCoO2电极有好的倍率放电性能,在3C倍率放电电压更高,放电比容量更高.原因可能如下:首先,MWCNTs、FNG和LiCoO2颗粒三者实现了均匀的分散;其次,MWCNTs把多个孤立的FNG联系起来,形成了更为有效的导电通道.
参考文献
| [1] | Whittingham M S .[J].Chemical Reviews,2004,104:4271-4301. |
| [2] | Robert R;Miran G;Jernej D et al.[J].Electrochimica Acta,2003,48:3709-3716. |
| [3] | Robert D;Miran G;Jernej D et al.[J].Journal of Power Sources,2003,119-121:770-773. |
| [4] | Jang DH.;Oh SM. .Effects of carbon additives on spinel dissolution and capacity losses in 4V Li/LixMn2O4 rechargeable cells[J].Electrochimica Acta,1998(9):1023-1029. |
| [5] | Momchilov A;Trifonova A;Banov B et al.[J].Journal of Power Sources,1999,81-82:566-570. |
| [6] | Qian L;John N H .[J].Journal of the Electrochemical Society,2004,151:A1115-A1119. |
| [7] | Indrajeet V T;Vipul M;John N H et al.[J].Journal of Power Sources,2006,162:673-678. |
| [8] | Li X L;Kang F Y;Shen W C .[J].Carbon,2006,44:1334-1336. |
| [9] | Kyuyun S;Young H L;Hong S L .[J].Journal of Power Sources,2006,158:1425-1430. |
| [10] | 王国平,张庆堂,瞿美臻,于作龙.纳米级碳导电剂的种类对LiCoO2电化学性能的影响[J].应用化学,2006(12):1385-1390. |
| [11] | Hong J K;Lee J H;Oh L S .[J].Journal of Power Sources,2002,111:90-96. |
| [12] | Cheon S E;Kwon C W;Kim D B et al.[J].Electrochimica Acta,2000,46:599-605. |
| [13] | 李志杰,梁奇,陈栋梁,瞿美臻,张伯兰,于作龙.碳纳米管和石墨在电化学嵌锂过程中的协同效应[J].应用化学,2001(04):269-271. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%