通过透射电镜(TEM)、扫描电镜(SEM)、光学显微镜(OM)和X射线衍射(XRD)手段,研究BT16钛合金丝材制备过程中微观组织演变、丝材的力学性能和冷镦性能以及固溶时效合金组织结构.结果表明:BT16合金丝材具有良好的力学性能,断面收缩率Ψ为62%~65%,顶镦螺栓头部变形量达到75%,未见任何缺陷.钛合金铸锭是树枝状α+β两相组织;锻坯横截面变形不均匀,析出等轴状、短棒状和针状α相;热锻棒材边界和晶内均有细小针状α相析出;丝材组织由初生等轴α相和β相组成;固溶时效后合金组织由初生等轴α相和析出针状α相的β转变组织组成.
参考文献
[1] | Ferrero J G .[J].Journal of Materials Engineering and Performance,2005,14(06):691. |
[2] | Skvortsov A A;Khabarov V P.[J].Metallovedenie i Termicheskaya Obrabotka Metallov,1988(10):56. |
[3] | Kolachev B A;Moiseev V N;Ryndenkov D V .[J].Metal Science and Heat Treatment,2006,48(5-6):240. |
[4] | 吴崇周.热镦对TC16钛合金组织和性能的影响[J].宇航材料工艺,2007(03):61-64. |
[5] | 辛社伟,赵永庆.关于钛合金热处理和析出相的讨论[J].金属热处理,2006(09):39-42. |
[6] | 沙爱学,王庆如,李兴无.BT16钛合金紧固件加工工艺分析[J].稀有金属材料与工程,2006(03):455-458. |
[7] | Li X W;Lu M X;Sha Ai X et al.[J].Materials Science and Engineering A,2008,490:193. |
[8] | Maltsev M V;Kashnikov N I.[J].Metallovedenie i Termicheskaya Obrabotka Metallov,1983(09):25. |
[9] | Urkhanov Y A;Rakhshtadt A G.[J].Metallovedenie i Termicheskaya Obrabotka Metallov,1996(07):16. |
[10] | Zong YY;Shan DB;Lu Y .Microstructural evolution of a Ti-4.5Al-3Mo-1V alloy during hot working[J].Journal of Materials Science,2006(12):3753-3760. |
[11] | Zhang Z G;Wu G Q;Song H et al.[J].Materials Science and Engineering A,2008,487:488. |
[12] | 张庆玲,王庆如,李兴无.航空用钛合金紧固件选材分析[J].材料工程,2007(01):11-14,18. |
[13] | 李兴无,沙爱学,储俊鹏,张雷,路民旭.淬火温度对Ti-3Al-4.5V-5Mo钛合金形变诱发马氏体的影响[J].材料工程,2007(09):3-8. |
[14] | Wang BF;Yang Y .Microstructure evolution in adiabatic shear band in fine-grain-sized Ti-3Al-5Mo-4.5V alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):306-311. |
[15] | Malitsev M V;Vokova T N;Skudnov V A .[J].Metallovedenie i Termicheskaya Obrabotka Metallov,1973,09:49. |
[16] | Kolachev B A;Mamonova F S .[J].Metallovedenie i Termicheskaya Obrabotka Metallov,1975,8:52. |
[17] | Luzhnikov L P;Novikova V M;Mareev V M .[J].Metallovedenie i Termicheskaya Obrabotka Metallov,1965,5:53. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%