阳极化处理对复合材料用导电铝箔网层耐蚀性的影响

腐蚀学报（英文）, 2011, 23(4): 342-345.

阳极化处理对复合材料用导电铝箔网层耐蚀性的影响

李娜 ^1, , 王志平 ^2, , 纪朝辉 ^3, , 王振良 ^4,

1.中国民航大学理学院,天津,300300

2.中国民航大学理学院,天津,300300

3.中国民航大学理学院,天津,300300

4.中国民航大学理学院,天津,300300

基金项目: 中国民航大学科研基金项目(2010kys05)

关键词：铝箔网 , 复合材料 , 磷酸阳极化 , 耐蚀性

Effect of Anodizing on Corrosion Resistance of Aluminum Foil Mesh of Conducting Layer for A1/CFRP Composite

Keywords： aluminum foil mesh , composite , phosphoric anodizing , corrosion resistance

为了提高铝箔网的耐腐蚀性能，采用磷酸阳极化方法对铝箔网表面进行处理．通过对磷酸阳极化后铝箔网的电化学极化腐蚀测试，优化铝箔网磷酸阳极化工艺；并对铝箔网及铝箔网导电层复合材料的耐环境腐蚀性能进行分析．结果表明：磷酸阳极化处理后铝箔网表面生成了一层疏松多孔的阳极氧化膜，使铝箔网的耐腐蚀性能得到提高；铝箔网／碳纤维层压板（CFRP）复合材料的粘接强度随腐蚀时间的延长而下降，而磷酸阳极化后铝箔网／碳纤维层压板复合材料的较未处理者有所提高．

A prerequisite is of proper corrosion performance for the aluminum foil mesh, which is an important component of the composite of aluminum foil mesh/carbon fiber reinforced polymer （CFRP） for aircraft. For enhancing its corrosion resistance, the aluminum foil mesh was anodized in solutions of phosphoric acid. The anodizing parameters were optimized by electrochemical polarization measurements. The environmental corrosion resistance of the anodized aluminum foil mesh and the composite with intercalation of aluminum foil mesh conducting layer was also examined. The result showed that： a porous film was formed on the surface of the anodized aluminum foil mesh, and it improved obviously the corrosion resistance of aluminum foil mesh. The shear strength of lap joint of composites aluminum foil mesh/carbon fiber reinforced polymer （CFRP） declined along with the corrosion time. The shear strength of lap joint of the composites intercalated with anodized aluminum foil mesh was better than that with bare aluminum foil mesh.

参考文献

[1]	Nunes de Souza L F, Librantz H, Amorim J. Analysis of direct effects of lightning on composite structures of air- craft [R]. Brazil: IX International Symposium on Light- ning Protection, 2007.
[2]	杜善义.先进复合材料与航空航天[J].复合材料学报,2007,24(1):1.
[3]	MIL-B-87162, Baffle material. Esplosion suppression ex- panded aluminum mesh for aircraft fuel tanks IS]. 1999.
[4]	Shebeko Y N. The new method for protection of tanks with flammable liquids against explosions[J]. 消防科学与技术, 2004, 5: 428.
[5]	GJB2639-96,军用飞机雷电防护[S].1996.
[6]	杨乃宾.复合材料飞机结构设计[M].北京:航空工业出版社,2002.
[7]	宋儒钧,王立广.关于提高复合材料中铝板基表面活性的研究[J].西安冶金建筑学院学报,1992,24(2):221.
[8]	Astrid B. Anodising as pre-treatment for structural bond- ing [J]. Int. J. Adhes., 2003, 23(5): 401.
[9]	Lunder O. Pre-treatment of AA6060 aluminium alloy for adhesive bonding [J]. Int. J. Adhes., 2002, 22(2): 143.
[10]	BSS7202, Shear, Lap, Adhesive Bond [S]. 1988.
[11]	朱祖芳.铝合金阳极氧化与表面处理技术[M].北京:化学工业出版社,2004.
[12]	钱苗根.现代表面技术[M].北京.机械工业出版社,2004.
[13]	杨孚标,肖加余,曾竟成等.铝合金磷酸阳极化和胶接性能分析[J].中国表面工程,2005,18(4):37.
[14]	Lu Y, Wu F, Xue G, et al. Interracial modification for an aluminum/epoxy resin laminated composite[J]. Compd. Interfaces. 1994, 2(4):265.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网