Polycarbonate (pc)/polypropylene (pp)/silicate attapulgite (AT) ternary nanocomposites were first prepared via the two-step melt blending process. Phase structure of the ternary composites was characterized by transmission electron microscopy (TEM) and dynamic mechanical analysis (DMA), in which the morphology of encapsulation of AT by PP in the PC matrix were observed. The mechanical properties of the ternary composites were investigated using the tensile tester and lzod impact tester. The results show that encapsulation of AT by PP in PC enhances the toughness of the matrix effectively and give the best tensile and impact strength.
参考文献
| [1] | Jie ZHOU;Ning LIU;Yun LI;Yijie MA.[J].Silicate Bulletin,1999(06):50. |
| [2] | M Tian;C D Qu;Y X Feng;L Q Zhang .[J].Journal of Materials Science,2003,38:4917. |
| [3] | H Haydy Murray .[J].Applied Clay Science,2000,17:207. |
| [4] | Z J Du;J F Romg;W Zhang;Z H Jing,H Q Li .[J].Journal of Materials Science,2003,38:4863. |
| [5] | Laurent Jayle;B Clive;Lvana K Partrige .[J].Polymer,1996,37(10):1897. |
| [6] | Y. H. Kim;M. Kikuchi;S. Akiyama;K. Sho;S. Izawa .Morphology and coarsening behavior in Polycarbonate/Nylon6-co-12 blends with and without compatibilizer[J].Polymer: The International Journal for the Science and Technology of Polymers,1999(19):5273-5278. |
| [7] | S A Xu;S C Tjong .[J].European Polymer Journal,1998,34(08):1143. |
| [8] | Z M Li;M B Yang;J M Feng;R Huang .[J].Journal of Materials Science,2001,36:2013. |
| [9] | P Sivaraman;N R Manoj;B C Chakraborty .[J].Polymer Testing,2004,23:527. |
| [10] | J P F Inberg;R J Gaymans .[J].POLYMER,2002,43:2425. |
| [11] | X B Hu;Alan J Lesser .[J].Polymer,2004,45:2333. |
| [12] | A L Hsieh;P Moy;F L Beyer .[J].Polymer Engineering and Science,2004,5:825. |
| [13] | R W Zong;Y Hu;S F Wang;R A Vaia .[J].Polymer Degradation and Stability,2004,83:423. |
| [14] | X Huang;S Lewis;W J Brittain;R A Vaia .[J].Macromolecules,2000,33:2000. |
| [15] | P.J.Yoon;D.R.Paul;D.L.Hunter .Polycarbonate nanocomposites: Part 2.Degradation and color formation[J].Polymer: The International Journal for the Science and Technology of Polymers,2003(18):5341-5354. |
| [16] | S F Wang;Y Hu;Z Z Wang;T Yong, Z Y Chen , W C Yan .[J].Polymer Degradation and Stability,2003,80:157. |
| [17] | K Premphet;P Horanont .[J].Polymer,2000,41:9283. |
| [18] | E J Sacher .[J].Journal of Macromolecular Sciences(Part B)Physics,1974,10(02):319. |
| [19] | J Kolaric;J Jancar .[J].POLYMER,1992,33:4961. |
| [20] | N Mekhilef;Ait A Kadi;A Ajji .[J].Polymer Engineering and Science,1992,32(13):894. |
| [21] | S Endo;K Min;L James .[J].Polymer Engineering and Science,1986,26(01):45. |
| [22] | S H Wu .[J].Polymer,1985,26(11):1855. |
| [23] | 冯威,毛立新,励杭泉,李齐方,武德珍,金日光.PPO/SEBS-g-MAH共混体系的冲击断面和微观形变过程[J].材料研究学报,2000(02):153-158. |
| [24] | Z M Li;M B Yang;W Yang .[J].Journal of Materials Science,2004,39:413. |
| [25] | Sz Molnar;B Pukanszky;C O Hammer .[J].Polymer,2000,41:1529. |
| [26] | K.T.Gam;M.Miyamoto;R.Nishimura;H.-J.Sue .Fracture Behavior of Core-Shell Rubber-Modified Clay-Epoxy Nanocomposites[J].Polymer engineering and science,2003(10):1635-1645. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%