用粉末冶金法制备了致密度较好的镀铜碳化硅增强铝基复合材料,并对碳化硅的表面化学镀工艺进行了分析.通过化学镀前后复合材料力学性能的对比研究表明,碳化硅表面镀铜较好地解决了碳化硅与基体的相容性问题,使复合材料的力学性能得到明显提高.
参考文献
[1] | Contreras A;Angeles-Chávez C;Flores O.Structural,morphological and interfacial characterization of Al-Mg/TiC composites[J].Materials Characterization,2007(58):685. |
[2] | Benji Maruyama;Warren H. Hunt Jr. .Discontinuously reinforced aluminum: current status and future direction[J].JOM,1999(11):59-61. |
[3] | 郝斌,段先进,崔华,杨滨,张济山.金属基复合材料的发展现状及展望[J].材料导报,2005(07):64-68. |
[4] | Weller M .The minimum volume fraction of SiC reinforcement required for strength improvement of Al-Cu based composite[J].Journal of Materials Science,1995,30(03):834. |
[5] | Kalogeropoulou S .Relationship between wettability and reactivity in SiCp Fe system[J].Acta Metallurgica Et Materialia,1995,43(03):907. |
[6] | Rui Zhang;Lian Gao;Jingkun Guo .Influence of Cu_2O on Interface Behavior of Copper/SiC_p Composite Prepared by Spark Plasma Sintering[J].Journal of the American Ceramic Society,2004(2):302-304. |
[7] | 李宁.化学镀实用技术[M].北京:化学工业出版社,2004 |
[8] | 赵伟,罗兵辉,柏振海.6066/SiCp复合材料最佳SiCp体积含量计算[J].轻合金加工技术,2007(05):38-40. |
[9] | 王国珍,丁雨田.SiC粒子增强铝基复合材料的断裂行为[J].甘肃工业大学学报,1998(01):1. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%