以聚苯乙烯微球(PS)为模板,采用“种子-生长”法在聚苯乙烯微球表面直接镀覆具有自支撑性的金壳层,成形热处理去除PS模板,成功制备出空心微球结构圆柱形块体的泡沫金样品,并对其制备工艺进行了研究.研究表明:平均晶粒尺寸为4.6 nm的金纳米粒子通过静电作用可成功粘附于交联聚苯乙烯微球(PS-DVB)表面.化学镀时以粘附的金纳米粒子为种子继续生长,沉积的金颗粒细小而致密,粒径主要分布于30～60 nm,且微球表面金沉积层的包覆率高,包覆厚度70～90 nm,PS模板去除后金沉积层具有良好的自支撑性.采用类似粉浆铸造工艺使gold/PS有孔隙地随机堆积成型,热处理去除聚苯乙烯模板后可成功获得圆柱体形状的泡沫金样品.制备的泡沫金由直径8～9 μm的空心球壳组成,圆柱体直径约4mm,密度约1.5 g/cm3,孔隙率高达92％.
参考文献
| [1] | Young P E;Rosen M D;Hammer J H et al.[J].Physical Review Letters,2008,101:035001. |
| [2] | Rosen Mordecai D;Hammer James H .[J].Physical Review E,2005,72:056403. |
| [3] | Nyce Gregory W;Hayes Joel R;Hamza Alex V et al.[J].Chemistry of Materials,2007,19:344. |
| [4] | Yoshio K;Yohei T;Daisuke No et al.[J].Journal of Colloid and Interface Science,2005,283(02):601. |
| [5] | Yong T L;O O Park;Hee-Tae J .[J].Journal of Colloid and Interface Science,2003,263(02):449. |
| [6] | Prokes S M;Carlos W E;Seals L et al.[J].Materials Letters,2002,54(01):85. |
| [7] | Yoshio K;Yerónica S M;Luis M L .[J].Chemistry of Materials,2001,13(05):1630. |
| [8] | Hayes J R;Nyce G W;Kuntz J D et al.[J].Nanotechnology,2007,18:275602. |
| [9] | David I. Gittins;Frank Caruso .Spontaneous Phase Transfer of Nanoparticulate Metals from Organic to Aqueous Media[J].Angewandte Chemie International Edition,2001(16):3001-3004. |
| [10] | 官建国,邓惠勇,王维,任平.以胶体粒子为模板制备核壳纳米复合粒子[J].化学进展,2004(03):327-334. |
| [11] | Kelly K L;Coronado E;Zhao L L et al.[J].Journal of Physical Chemistry B,2003,107:6682677. |
| [12] | 吴泓橙,董守安,董颖男,唐春,杨生春.金纳米粒子的阳光光化学合成和晶种媒介生长[J].高等学校化学学报,2007(01):10-15. |
| [13] | Kan C;Cai W;Li C et al.[J].Journal of Materials Research,2005,20(02):320. |
| [14] | 曾文茹,周允基,霍然,姚斌,李元洲.非等温动力学积分-微分法研究聚苯乙烯热解反应机理及动力学参数[J].高分子材料科学与工程,2006(05):162-165. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%