The prepolymer polyurethanes(PUs)based on isophorone diisocyanate(IPDI),poly(propylene glycol)(PPG),1,4-butanedioi(BDO)and dimethylopropionic acid(DMPA)were synthesized at 75-80℃ for 7-8 hours,using dibutyltin dilauate(DBTDL)as catalyzer,and polyturethane-acrylate hybrid emulsion was prepared after methyl methacrylate(MMA)was polymerized,using potassium persulfate and azobisisobutyronitrile(AIBN)as initiator,respectively.The influences of these factors such as the kind of initiator,the feed method of initiator and the addition of initiator on properties of polyurethane-acrylate were studied.The FTIR and GPC of aqueous polyurethane were analyzed.The FTIR spectra show that the degree of microphase-separate between the soft segments and rigid segments is high.The analysis of molecular weights stated that molecular weights increased most significantly after amine was added.The experimental results reveal that the appearance of emulsion is excellent,the film is harder and the water absorption radio of the film is less when oil-solubility AIBN is used as initiator.The semi-continuous can increase the molecular weight of polymer and the optimum amount of the initiator was 3% for MMA.
参考文献
| [1] | Yeganeh H;Mehdizadeh MR .Synthesis and properties of isocyanate curable millable polyurethane elastomers based on castor oil as a renewable resource polyol[J].European Polymer Journal,2004(6):1233-1238. |
| [2] | Coutinho FMB.;Delpech MC. .SOME PROPERTIES OF FILMS CAST FROM POLYURETHANE AQUEOUS DISPERSIONS OF POLYETHER-BASED ANIONOMER EXTENDED WITH HYDRAZINE[J].Polymer Testing,1996(2):103-113. |
| [3] | Riadh Elleuch;Khaled Elleuch;Boudour Salah .Tribological behavior of thermoplastic polyurethane elastomers[J].Materials & Design,2007(3):824-830. |
| [4] | G N Chen;K N Chen .Self-curing Behaviors of Single Pack Aqueous-based Polyurethane Systems[J].Apple Polymer Science,1997,63(12):1609-1623. |
| [5] | Brown RA;Coogan RG;Fortier DG;Reeve MS;Rega JD .Comparing and contrasting the properties of urethane/acrylic hybrids with those of corresponding blends of urethane dispersions and acrylic emulsions[J].Progress in Organic Coatings: An International Review Journal,2005(1):73-84. |
| [6] | Xingjun Lu;Mingshan Hou;Xiuxiang Gao et al.Investigation of Interactions in Polyether-polyurethanes and Their Mixtureswith Other Polyurethanes by High Resolution NMR[J].Polymer,1994,35(12):2510-2515. |
| [7] | M C Delpech;F M B Coutinho .Waterborne Anionic Polyurethane and Poly(urethane-urea)s:Influence of the Chain Extender on Mechanical and Adhesive Properties[J].Polymer Testing,2002,19(08):939-952. |
| [8] | Hamid Yeganeh;Moslem Mansour Lakouraj;Sadegh Jamshidi .Synthesis and Properties of Biodegradable Elastomeric Epoxy Modified Polyurethanes Based on Poly(ε-caprolactone)and Poly(ethylene glycol)[J].European Polymer Journal,2004,41(10):2370-2379. |
| [9] | Jeevananda T.;Siddaramaiah. .Synthesis and characterization of polyaniline filled PU/PMMA interpenetrating polymer networks[J].European Polymer Journal,2003(3):569-578. |
| [10] | Pan Zu-ren.Polymer Chemistry[M].北京:化学工业出版社,1997:24-31. |
| [11] | A.M.Imroz Ali;Klaus Tauer;Milos Sedlak .Comparing emulsion polymerization of methacrylate-monomers with different hydrophilicity[J].Polymer: The International Journal for the Science and Technology of Polymers,2005(4):1017-1023. |
| [12] | 聂华荣,陈义旺,贺晓慧,邹鑫.聚氯甲基苯乙烯纳米乳胶粒子的制备[J].应用化学,2006(05):498-502. |
| [13] | Scorah MJ;Dhib R;Penlidis A .Modelling of free radical polymerization of styrene and methyl methacrylate by a tetrafunctional initiator[J].Chemical Engineering Science,2006(15):4827-4859. |
| [14] | Cao Yutong;Liu Qingpu;Hu Jinsheng.The Synthesized Principle and Application of Polymer[M].北京:化学工业出版社,1997:19-24. |
| [15] | Hong Liang .Synthesis of Polyurethane-acrylate Hybrid Emulsion[D].广州:华南工业大学,2003. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%