制备了低成本工程机械用550MPa级钢,研究了轧后超快冷工艺对该钢组织与性能的影响。结果表明：超快冷工艺有效提高了该钢的力学性能,其屈服强度、抗拉强度和断后伸长率分别可达600MPa,755MPa,19%,-20℃的冲击功为253J;超快冷后钢的组织为贝氏体,其强化相为细小的贝氏体及基体中分布着的细小析出相。
A kind of 550 MPa steel used for engineering machinery with low cost was prepared,and the effects of ultra fast cooling process after rolling on microstructure and mechanical property of the steel were studied.The results show that the ultra fast cooling process could increase the properties of the steel effectively,and the yield strength,tensile strength,elongation and impact energy at-20 ℃ were 600 MPa,755 MPa,19% and 253 J,respectively.The microstructure of the steel after ultra fast cooling was bainite,and the reinforcement phases were fine bainite and fine precipitation distributing in matrix.
参考文献
| [1] | D.C. Foley;M. Al-Maharbi;K.T. Hartwig .Grain refinement vs. crystallographic texture: Mechanical anisotropy in a magnesium alloy[J].Scripta materialia,2011(2):193-196. |
| [2] | 关绍康,王迎新.高温镁合金的研究进展及其在汽车工业中的应用[J].机械工程材料,2003(08):1-4. |
| [3] | Ming-Hung Tsai;May-Show Chen;Ling-Hung Lin .Effect of heat treatment on the microstructures and damping properties of biomedical Mg-Zr alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2011(3):813-819. |
| [4] | 杨光昱,介万奇,郝启堂.Mg-5Zn-3Al-0.2Mn铸造合金的组织和室温力学性能[J].中国有色金属学报,2006(02):205-212. |
| [5] | 郭学锋,杨文朋,宋佩维.往复挤压Mg-4Al-2Si合金的高温拉伸性能[J].中国有色金属学报,2010(06):1032-1038. |
| [6] | M. Mabuchi;H. Iwasaki;K. Yanase;K. Higashi .LOW TEMPERATURE SUPERPLASTICITY IN AN AZ91 MAGNESIUM ALLOY PROCESSED BY ECAE[J].Scripta materialia,1997(6):681-686. |
| [7] | 徐春杰,郭学锋,张忠明,贾树卓,刘礼.往复挤压及正挤压AZ91D镁合金丝材的组织及性能[J].稀有金属材料与工程,2007(03):500-504. |
| [8] | 金文中,刘顺华.镁合金焊丝的热挤压-拉拔工艺及其变形机理[J].材料科学与工艺,2005(05):466-469. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%