采用水/环己烷/TritonX-100/正己醇四元油包水体系,通过微乳液法制备了纳米ZrO2粉体,用XRD、TEM、TG-DTA等对所制备的纳米粉体进行了表征,并重点研究了体系中增溶的锆盐溶液浓度对ZrO2纳米粒子结构与性能的影响.结果表明,本方法所制备的纳米单斜相ZrO2粉体,其晶粒尺寸可控制在15 nm左右;在479℃左右,纳米粉体由无定形转变为晶相;在较低的煅烧温度下,所合成的氧化锆粒子中同时存在着单斜相和四方相两种晶粒,随着煅烧温度的提高,部分四方相会转变为单斜相,到煅烧温度为800℃时,几乎全部转化为单斜相;随着锆盐浓度的增加,所合成粉体的晶型没有太大的变化,均为单斜相,但是晶体结构的完整性略有不同;随着锆盐浓度的增加,所合成粉体的晶粒尺寸有所增大,团聚现象亦有所加重.
参考文献
| [1] | Joo J.;Yu T.;Kim YW.;Park HM.;Wu FX.;Zhang JZ.;Hyeon T. .Multigrarn scale synthesis and characterization of monodisperse tetragonal zirconia nanocrystals[J].Journal of the American Chemical Society,2003(21):6553-6557. |
| [2] | YU Jian-Chang,HU Sheng-Wei.Synthesis and Characterization of Zirconia Nanocrystallites by Cationic Surfactant and Anionic Surfactant[J].结构化学,2005(10):1133-1139. |
| [3] | Kikkawa S;Kijima A;Hirota K et al.[J].Journal of the American Ceramic Society,2002,85(03):721. |
| [4] | 黄传勇,唐子龙,张中太.纳米级二氧化锆粉体合成新方法[J].硅酸盐学报,2000(01):11-14. |
| [5] | 王和义,傅依备.沉淀-乳化法制备二氧化锆纳米粉末技术研究[J].硅酸盐通报,1999(05):66-68. |
| [6] | 崔若梅;张文礼;徐中理.[J].化学世界,1999(12):630. |
| [7] | Deliang Chen .[J].Journal of Crystal Growth,2004,262:554. |
| [8] | Qiu S;Dong J;Chen G J .[J].Journal of Colloid and Interface Science,1999,216(02):230. |
| [9] | Eel L S;Wang J;Ng S C et al.[J].Materials Research Bulletin,1998,33(07):1045. |
| [10] | Jiye Fang;Kevin L;Stokes et al.[J].Materials Letters,2000,42:113. |
| [11] | John Wang;Jiye Fang;Ser-Choon Ng;Leong-Ming Gan;Chwee-Har Chew;Xianbin wang;Zexiang Shen .Ultrafine barium titanate powders via microemulsion processing routes[J].Journal of the American Ceramic Society,1999(4):873-881. |
| [12] | Clifford Y Tai;Bor-Yuan Hsiao;Hsien-Yi Chiu .[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2004,237:105. |
| [13] | 杨絮飞,黎维彬.在水/环己烷微乳体系中制备纳米级氧化锆微粒[J].物理化学学报,2002(01):5-9. |
| [14] | 论普遍伦理的根本目标和哲学基础[J].深圳大学学报(人文社会科学版),2001(01):50. |
| [15] | Bokhimi X;Morales A;Garcia-Ruiz A et al.[J].Journal of Solid State Chemistry,1999,142:409. |
| [16] | Huang Y Y;Zhao B Y;Xie Y C .[J].Applied Catalysis A:General,1998,171(01):75. |
| [17] | Mekhemer;Gamal A H;Ismail H M .[J].Colloids and Surfaces,2000,164(02):227. |
| [18] | Liang K;Gu K;Gu S et al.[J].Journal of the Chinese Ceramic Society,1995,23(05):447. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%