研究了经磨盘形力化学反应器碾磨处理后的PVC/SBS共混体系的结构与性能.结果表明,经过碾磨的PVC/SBS共混体系的GPC曲线峰型变宽,峰位向高分子量部分移动,Molau实验和FT-IR均表明在碾磨过程中有PVC-SBS共聚物生成,SBS与PVC的相容性得到了改善.PVC的冲击强度为4.6 kJ/m2,以PVC与SBS共碾磨产物(MCB)为增容增韧剂可使PVC/MCB(100/59)的冲击强度高达68.1 kJ/m2.少量超细CaCO3的加入可提高共混体系的屈服强度和断裂伸长率,通过碾磨可获得既增韧又增强的良好效果.