利用歧化反应原理,在SiC颗粒表面包覆金属Cu.通过俄歇电子能谱(AES),分析粒度分布对Cu包覆SiC颗粒相分布均匀性的影响.SiC颗粒的粒度分布范围过宽,Cu倾向于包覆在大颗粒表面而无法分散到细小颗粒表面.减小粒度分布范围,纳米SiC颗粒同样能被Cu均匀包覆.应当控制纳米SiC颗粒在一个较小的分布范围,以保证理想的Cu包覆效果和两相分散均匀性.
Based on the disproportionation reaction, SiC particles were coated with Cu. AES technology was carried out to determine the influence of size-distribution on the phase homogeneity between SiC and Cu. Cu tends to deposit on the large particles rather than on the very fine coexisted particles in a wide size-distribution powders. Nano SiC particles can be coated readily with the narrow particle size- distribution, which leads to the desired phase homogeneity.
参考文献
| [1] | Harmer M A, Bergna H, Saltzberg M, et al. J. Am. Ceram. Soc., 1996, 79 (6): 1546--1552. [2] Shih W H, Kisailus D, Shih W Y, et al. J. Am. Ceram. Soc., 1996, 79 (5): 1155--1162. [3] Han K R, Lim C S, Hong M J, et al. J. Am. Ceram. Soc., 1996, 79 (2): 574--576. [4] Djuricic B, Mcgarry D, Pickering S. J. Mater. Sci. Lett., 1993, 12: 1320--1323. [5] Lee H K, Kin K Y. J. Mater. Sci. Lett., 1994, 13: 1149--1150. [6] Wang C M, Zhe X L. J. Mater. Sci. Lett., 1995, 14: 129--131. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%