对Mg-Mn-RE合金进行挤压和锻造变形处理,研究不同变形方式对其显微组织及力学性能的影响.结果表明:合金挤压变形过程中发生了动态再结晶,晶粒明显细化,挤压变形后硬度、抗拉强度、屈服强度和伸长率相对于铸态都有所提高,分别为68HV、254.9 MPa、190.5 MPa和26%;室温锻造变形后,晶粒扭曲变形,稀土化合物呈弥散均匀分布,硬度相对于挤压变形后有所提高,相对变形量为28%时,合金硬度为101 HV.
参考文献
| [1] | Luo A;Pekgnleryuz M O .Cast magnesium alloys for elevated temperature applications[J].Journal of Materials Science,1994,29(20):5259-5271. |
| [2] | Fang, D.;Bi, G.;Wang, L.;Li, G.;Jiang, Z. .Microstructures and mechanical properties of Mg-2Y-1Mn-1-2Nd alloys fabricated by extrusion[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(16/17):4383-4388. |
| [3] | WANG Qiang,高家诚,WANG Yong,李伟,NIU Wen-juan.均匀化退火对WE43镁合金铸坯组织和性能的影响[J].材料热处理学报,2008(04):65-68. |
| [4] | YU Kun;LI Wen-xian;WANG Ri-chu .Mechanical properties and microstructure of as-cast and extruded Mg-(Ce, Nd)-Zn-Zr alloys[J].Journal of Central South University of Technology,2005(5):499-502. |
| [5] | 刘喜明.冷却方式对Mg-Nd-Pr合金的显微组织与物相构成的影响[J].稀有金属材料与工程,2009(04):677-680. |
| [6] | 李德君,刘平,董企铭,田保红,任凤章.Mg-3Al-1Zn-0.8Nd合金热压缩变形流变应力的研究[J].材料热处理学报,2008(05):26-30. |
| [7] | 熊创贤,张新明,陈健美,邓运来,邓桢桢.Mg-Gd-Y-Mn耐热镁合金的压缩变形行为研究[J].材料热处理学报,2007(03):47-53. |
| [8] | Ogawa N;Shiomi M;Osakada K .Forming limit of magnesium alloy at elevated temperature for precision forging[J].Machine Tools and Manufacture,2002,42(05):607-614. |
| [9] | 曹凤红,龙思远,杜勇,张广俊.AZ61镁合金挤锻复合成形组织与力学性能[J].材料热处理学报,2009(05):154-157. |
| [10] | 杜勇,龙思远,曹凤红,常欢欢.挤锻复合成形工艺对AZ81镁合金组织和性能的影响[J].特种铸造及有色合金,2009(01):39-41. |
| [11] | J. F. Nie and B. C. Muddle .CHARACTERISATION OF STRENGTHENING PRECIPITATE PHASES IN A Mg-Y-Nd ALLOY[J].Acta materialia,2000(8):1691-1703. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%