采用溶胶-凝胶法合成了Yb：GGG多晶料.以XRD分析方法对合成料的前驱体及烧成的粉体的相结构进行了研究,XRD分析结果表明,950 ℃煅烧的粉体已是Yb:GGG纯相.采用提拉法,通过设计合理而稳定的温场、选择最佳工艺参数等生长了Yb:GGG晶体.荧光光谱测试结果表明,Yb:GGG晶体主要发射峰位于1030 nm,该荧光是由Yb3+激发态2F5/2向基态2F7/2能级跃迁产生的.
参考文献
| [1] | Lacovara P;Choi H K;Wang C A et al.Room-temperature diode-pumped Yb:YAG lasers[J].Optics Letters,1991,16(14):1089-1091. |
| [2] | Qiu H W;Yang P Z;Dong J et al.The influence of Yb concentration on laser crystal Yb:YAG[J].Materials Letters,2002,55(01):1-7. |
| [3] | 张庆礼,殷绍唐,王爱华,肖敬忠.GGG系列激光晶体研究进展[J].量子电子学报,2002(06):481-484. |
| [4] | Jiang BX;Zhao ZW;Xu XD;Song PX;Wang XD;Xu J;Deng PZ .Spectral properties and charge transfer luminescence of Yb3+ : Gd3Ga5O12 (Yb : GGG) crystal[J].Journal of Crystal Growth,2005(1/4):186-191. |
| [5] | Benxue Jiang;Zhiwei Zhao;Xiaodong Xu .Visible luminescence in Yb~(3+)-doped gadolinium gallium garnets[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2007(1/3):20-23. |
| [6] | 孙晶,刘景和,关效贤,李建利,曾繁明,万玉春,张亮.Nd：Gd3Ga5O12多晶原料合成及单晶生长研究[J].硅酸盐学报,2004(05):585-589. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%