采用光学显微镜、XRD等手段研究了脉冲电流处理对过共晶高铬铸铁凝固过程中初生碳化物的尺寸、形态和种类的影响.结果表明:脉冲电流能够细化过共晶高铬铸铁中初生碳化物和共晶碳化物,初生碳化物由长杆状转化成规则的块状.不同温度区间内脉冲电流对初生碳化物影响效果不同,合金液相线以上(1360 ～1337℃)脉冲电流处理更有利于细化初生碳化物,细化效果最好,凝固全过程处理次之(1360 ～ 1276 ℃),液固区间处理效果最差(1337～ 1276℃).
参考文献
| [1] | Carpenter, SD;Carpenter, D;Pearce, JTH.XRD and electron microscope study of an as-cast 26.6% chromium white iron microstructure[J].Materials Chemistry and Physics,20041(1):32-40. |
| [2] | 王均;曾明;杨宏山;刘浩怀;孙志平;沈保罗;黄四九.不同热处理对一种高铬铸铁组织的影响[J].材料热处理学报,2005(6):75-79. |
| [3] | Carpenter SD;Carpenter D;Pearce JTH.XRD and electron microscope study of a heat treated 26.6% chromium white iron microstructure[J].Materials Chemistry and Physics,20071(1):49-55. |
| [4] | 周荣锋;陈华;王铁旦;张玲;蒋业华;周荣.脉冲电流作用下高铬铸铁中碳化物形貌变化[J].材料热处理学报,2011(7):57-61. |
| [5] | Xiaohui Zhi;Jinzhi Liu;Jiandong Xing;Shengqiang Ma.Effect of cerium modification on microstructure and properties of hypereutectic high chromium cast iron[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2014:98-103. |
| [6] | Jun Wang;Cong Li;Haohuai Liu.The precipitation and transformation of secondary carbides in a high chromium cast iron[J].Materials Characterization,20061(1):73-78. |
| [7] | Zhifu HUANG;Jiandong XING;Anfeng ZHANG.Microstructure and Property of Hypereutectic High Chromium Cast Iron Prepared by Slope Cooling Body-Centrifugal Casting Method[J].材料科学技术学报（英文版）,2006(06):775-778. |
| [8] | 何树先;王俊;周尧和.高密度脉冲电流对A356铝合金低温熔体凝固组织的影响[J].金属学报,2002(5):479-482. |
| [9] | 赵远云;王宝全;郭敬东.高密度脉冲电流处理改善1Cr13Mn13钢力学性能[J].金属学报,2009(11):1325-1329. |
| [10] | 何树先 .铝合金的熔体温度处理和电脉冲处理研究[D].上海交通大学,2002. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%