采用溶胶-凝胶法在45钢表面制备了Al2O3陶瓷涂层,研究了通过化学镀Ni-P层为中间过渡层对45钢表面Al2O3陶瓷涂层性能的影响.通过压入法和划痕法研究了膜基结合强度,观察了复合涂层压痕和划痕形貌,通过扫描电子显微镜(SEM)对复合涂层表面形貌进行了分析.结果表明,中间层与基体材料、Al2O3层与中间层结合良好,涂层均匀致密,表面显微硬度最大值为1030HV,压入法结果表明膜与45钢基体结合较好.
参考文献
| [1] | 姚明明,缑英俊,何业东.高温防护涂层研究进展[J].中国粉体技术,2005(03):32-37,43. |
| [2] | Haibin Li;Kaiming Liang;Lefu Mei .Oxidation protection of mild steel by zirconia sol-gel coatings[J].Materials Letters,2001(4):320-324. |
| [3] | 李良坚,何业东,王德仁.Sol-gel热压法制备Al2O3-Y2O3复合陶瓷涂层及其抗高温氧化性能[J].材料热处理学报,2005(06):101-104. |
| [4] | Fedrizzi L;Rodriguez F J;Ressi S et al.The use of electrochemical techniques to study the corrosion behnviour of organic coatings on steel pretreated with sol-gel zirconia films[J].Electrechimica Acta,2001,46:3715-3724. |
| [5] | Ruhi G;Modi OP;Singh IB;Jha AK;Yegneswaran AH .Wear and electrochemical characterization of sol-gel alumina coating on chemically pre-treated mild steel substrate[J].Surface & Coatings Technology,2006(3/4):1866-1872. |
| [6] | Zhou MH;Yang QZ;Troczynski T .Effect of substrate surface modification on alumina composite sol-gel coatings[J].Surface & Coatings Technology,2006(8):2800-2804. |
| [7] | Ezz T;Crouse P;Li L;Liu Z .Synthesis and coating of micro-metal-matrix composite by combined laser sol-gel processing[J].Surface & Coatings Technology,2007(12):5809-5814. |
| [8] | Heinke W;Leyland A;Matthews A .Evaluation of PVD nitride coatings,using impact,scratch and Rockwell-c adhesion test[J].Thin Solid Films,1995,270:431-438. |
| [9] | 张际亮 .铝基硅氧化物陶瓷膜层制备、性能与机理研究[D].杭州:浙江大学,2008. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%