本文研究了高温作用后玄武岩纤维高强混凝土的力学性能随温度和纤维掺量的变化规律.结果表明:高温后玄武岩纤维高强混凝土(BHSC)质量损失随温度的升高而逐渐增大;抗压强度随温度的升高呈现先增大后减小的趋势,200℃后强度略有增加;峰值应变随温度的升高而大幅增大,400℃和600℃后尤为明显;峰值韧性随着温度的升高显著提高,200℃时最为明显;常温、400℃和600℃时玄武岩纤维对高强混凝土峰值韧性的改善效果较为明显.0.2％为相对最优向纤维掺量.
参考文献
| [1] | Kazuo Watanabe;Mugume Rodgers Bangi;Takashi Horiguchi.The effect of testing conditions (hot and residual) on fracture toughness of fiber reinforced high-strength concrete subjected to high temperatures[J].Cement and Concrete Research,2013:6-13. |
| [2] | Mitsuo Ozawa;Shinya Uchida;Toshiro Kamada;Hiroaki Morimoto.Study of mechanisms of explosive spalling in high-strength concrete at high temperatures using acoustic emission[J].Construction and Building Materials,2012:621-628. |
| [3] | 林熙,季锡贤,殷新博,吴媛媛.C60～C100高强混凝土强度尺寸效应的研究[J].硅酸盐通报,2013(10):2090-2093. |
| [4] | 牛旭婧,赵庆新,陈天红.聚丙烯粗纤维对高强混凝土高温后性能影响[J].硅酸盐通报,2013(12):2583-2588. |
| [5] | 高丹盈,李晗,杨帆.聚丙烯-钢纤维增强高强混凝土高温性能[J].复合材料学报,2013(01):187-193. |
| [6] | 金凤杰,许金余,范飞林,苏灏扬.钢纤维混凝土的高温动态强度特性[J].硅酸盐通报,2013(04):683-686. |
| [7] | 李为民,许金余,沈刘军,李庆.玄武岩纤维混凝土的动态力学性能[J].复合材料学报,2008(02):135-142. |
| [8] | 邓宗才,薛会青.玄武岩纤维混凝土的抗弯冲击性能[J].建筑科学与工程学报,2009(01):80-83. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%