介绍了利用非水溶液电解法提取薄带连铸低碳钢中氧化物夹杂的方法,采用带有EDS系统的扫描电镜(SEM)研究了氧化物夹杂的三维形貌和化学成分,并通过热力学计算获得控制低熔点夹杂物生成所需成分范围.结果表明:低熔点Al2O3-SiO2-MnO类夹杂物三维形貌为球形;随着钢液中酸溶铝含量的增加,夹杂物中Al2O3含量相应地增加,当钢液中[％C]=0.10、[％Si]=0.35、[％Mn]=0.90、夹杂物的熔点控制在1 200℃范围时,要求钢液中的酸溶铝含量很低,需控制在(1～5) ×10-6.
参考文献
| [1] | Shibuya K;Ozawa M .Strip Casting Techniques for Steel[J].ISIJ International,1991,31(07):661-668. |
| [2] | 潘秀兰;王艳红;梁慧智.薄带铸轧技术现状与展望[J].冶金信息导刊,2009(02):5-8. |
| [3] | R.P.Tavares .Roll-strip Interfacial Heat Fluxes in Twin-roll Casting of Low-carbon Steels and Their Effects on Strip Microstructure[J].ISIJ International,1998(12):1353-1360. |
| [4] | Jae Young P;Oh K H;Ra H Y .The Effects of superheating on texture and microstructure of Fe-4.5wt％ Si steel strip by twinroll strip casting[J].ISIJ International,2001,4(01):70-75. |
| [5] | A.Girgensohn;A.R.Buchner .Twin roll strip casting of low carbon steels[J].Ironmaking & Steelmaking: Products and applications,2000(4):317-323. |
| [6] | Cook R;Grocock P;Thomas P et al.Development of the twinroll casting process[J].Journal of Materials Processing Technology,1995,55(02):76-84. |
| [7] | 陈家祥.炼钢常用图表数据手册[M].北京:冶金工业出版社,1984:383-391. |
| [8] | 薛正良,李正邦,张家雯,甘朝福,王玉.改善弹簧钢中氧化物夹杂形态的热力学条件[J].钢铁研究学报,2000(06):20-24. |
| [9] | 黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,2002 |
| [10] | 刘健,郑少波,蒋国昌.MnO-SiO2二元系SELF-SReM模型及应用[J].钢铁研究学报,2006(05):18-21,59. |
| [11] | 蒋国昌,徐匡迪.高阶亚正规熔体模型[J].中国有色金属学报,2002(05):1040-1049. |
| [12] | 张晓兵;蒋国昌 .高阶亚正规溶液模型及其在MnO-SiO2-Al2O3-CaO炉渣中组元活度[J].金属学报,1997,33(10):1085-1093. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%